Pilot-scale manufacturing of phase-pure and highly crystalline hydroxyapatite: Lessons learned and process protocols

Barui, S and Hadagalli, K and Mukherjee, S and Roy, S and Bhattacharjee, D and Basu, B (2022) Pilot-scale manufacturing of phase-pure and highly crystalline hydroxyapatite: Lessons learned and process protocols. In: International Journal of Applied Ceramic Technology, 19 (2). pp. 762-772.

PDF int_jou_app_cer_tec_19-2_762-772_2022.pdf - Published Version Restricted to Registered users only Download (4MB) | Request a copy

Abstract

The recognition of hydroxyapatite (HAp) as the major bone mineral triggered significant research in bone tissue engineering applications. Although laboratory-scale development involves the synthesis of HAp in different routes, scalability with uncompromised quality remains a major challenge. This article reports a large-scale wet precipitation-based synthesis of phase-pure HAp using indigenously customized stirred tank reactors. The different synthesis parameters, like pH, reaction time, stirring rate, precursor addition, were tailored, together with the post-synthesis mechano-chemical treatment (aging induced Ostwald ripening) and calcinations, as the technology is matured to manufacture HAp powders in large volume. At least three batches of HAp were produced in the pilot-scale reactor with reproducible values of phase purity, compositional fingerprint, particle size distribution, flowability, etc. The post-calcination bluish tint was strategically addressed by adopting a proprietary calcination protocol. This batch process can produce around 200 kg/month of phase-pure and highly crystalline (91–94%) HAp using stirred tank reactors of different working volumes. Extensive scanning electron microscopy (SEM) and transmission electron microscopy (TEM) analyses reveal the particle size of as-synthesized HAp powders with hexagonal crystal structure in the range of 20.47 ± 4.95 nm, while individual crystallite size in range of 22.3 ± 3.2 nm (XRD based Debye-Scherrer analysis). TEM-based SADP analysis confirms the highly crystalline hexagonal structure of as-synthesized HAp. The spray-dried powders with spherical shape having narrow size distribution (35–40 μm) could also be manufactured in large batches. The spray-dried HAp powders could be coated on clinically used stainless steel femoral stem implants using atmospheric plasma spray coating technique.

Item Type:	Journal Article
Publication:	International Journal of Applied Ceramic Technology
Publisher:	John Wiley and Sons Inc
Additional Information:	The copyright for this article belongs to the John Wiley and Sons Inc.
Keywords:	Batch data processing; Calcination; Chemical analysis; Crystal structure; Crystallite size; Emulsification; High resolution transmission electron microscopy; Hydroxyapatite; Ostwald ripening; Particle size; Particle size analysis; Powders; Scanning electron microscopy; Size distribution; Spray drying; Tanks (containers); Tissue engineering, Crystalline hydroxyapatite; Hydroxyapatite powder; Implant coating; Phase pure; Pilot scale; Process protocol; Spray-drying; Stirred-tank reactors; Synthesised; Wet precipitation, Coatings
Department/Centre:	Division of Chemical Sciences > Materials Research Centre Division of Interdisciplinary Sciences > Centre for Biosystems Science and Engineering
Date Deposited:	13 Dec 2021 11:38
Last Modified:	30 Jun 2022 05:23
URI:	https://eprints.iisc.ac.in/id/eprint/70759

Actions (login required)

View Item