Effect of heat treatment on microstructure and high-temperature wear performance of additive manufactured IN718

S, CS and Prabhu, TR and Moganraj, A and Samuel, MS and Praveenkumar, K and Bobby, SS and Prakasam, A (2024) Effect of heat treatment on microstructure and high-temperature wear performance of additive manufactured IN718. In: Journal of Manufacturing Processes, 127 . pp. 683-697.

PDF Jou_man_pro_127_2024.pdf - Published Version Restricted to Registered users only Download (24MB) | Request a copy

Abstract

The additive manufactured IN718 under Laser Powder Bed Fused (LPBF) was evaluated for its microstructure, microhardness, and wear behavior in both as-printed and precipitation heat-treated condition. The microstructure of as-print IN718 shows slender columnar dendrites oriented directionally along build direction and coarse cellular structure in the remelt zone that formed between the laser-deposited tracks. After solution double aging heat treatment (AMS 5662), reinforcing precipitates (γ� and γ�) were observed in the γ-matrix and δ-phase precipitation at grain boundaries. Microhardness analysis indicates that the alloy's hardness was improved and stabilized in all direction after the heat treatment. The alloy's tribological behavior was examined at temperatures of 28 °C, 400 °C, 500 °C, and 600 °C in a pin on disc setup. SEM and XRD analyses were used to examine the worn-out surface and wear debris. Surface examination of the worn-out sample reveals abrasion wear at 28 °C and delamination wear at 400 °C, 500 °C and 600 °C. The topography study highlights that abrasion and delamination wear are considerably reduced after heat-treatment. The friction coefficient and wear loss increase with the test temperature indicates that delamination plays a crucial role in affecting both friction and wear loss. XRD analysis on the worn-out surface detected nickel oxide (NO) formation in all high temperature tested samples and the NiO is ineffective in reducing friction and wear loss. The sectional analysis of worn-out surface shows noticeable variations in delamination intensity as the test temperature rises. A thorough examination of the wear debris reveals delamination marks on the front surface and micro-cracks developing on the back surface. The microstructure examination carried out near the worn-out surface of both as-printed and heat-treated sample tested at 600 °C. The analysis confirmed excess δ-phase formation at the grain boundary of as-printed sample aggravates crack propagation and wear loss due to delamination. © 2024 The Society of Manufacturing Engineers

Item Type:	Journal Article
Publication:	Journal of Manufacturing Processes
Publisher:	Elsevier Ltd
Additional Information:	The copyright for this article belongs to the publisher.
Keywords:	After-heat treatment; Crack propagation; Heat affected zone; Microhardness; Nickel alloys, Aging heat treatment; Delamination wear; Double aging; Grain-boundaries; High temperature wear; Laser powder bed fusion; Laser powders; Powder bed; Solution double aging heat treatment; Wear loss, Abrasion
Department/Centre:	Division of Mechanical Sciences > Department of Design & Manufacturing (formerly Centre for Product Design & Manufacturing) Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited:	15 Sep 2024 10:01
Last Modified:	15 Sep 2024 10:01
URI:	http://eprints.iisc.ac.in/id/eprint/86069

Actions (login required)

View Item