Kumar, Arvind and Mondal, Sandip and Rao, Koteswara KSR (2015) DLTS analysis of amphoteric interface defects in high-TiO2 MOS structures prepared by sol-gel spin-coating. In: AIP ADVANCES, 5 (11).
|
PDF
AIP_Adv_5-11_117122_2015.pdf - Published Version Download (3MB) | Preview |
Abstract
High-kappa TiO2 thin films have been fabricated from a facile, combined sol-gel spin - coating technique on p and n type silicon substrate. XRD and Raman studies headed the existence of anatase phase of TiO2 with a small grain size of 18 nm. The refractive index `n' quantified from ellipsometry is 2.41. AFM studies suggest a high quality, pore free films with a fairly small surface roughness of 6 angstrom. The presence of Ti in its tetravalent state is confirmed by XPS analysis. The defect parameters observed at the interface of Si/TiO2 were studied by capacitance - voltage (C - V) and deep level transient spectroscopy (DLTS). The flat - band voltage (V-FB) and the density of slow interface states estimated are -0.9, -0.44 V and 5.24x10(10), 1.03x10(11) cm(-2); for the NMOS and PMOS capacitors, respectively. The activation energies, interface state densities and capture cross -sections measured by DLTS are E-V + 0.30, E-C - 0.21 eV; 8.73x10(11), 6.41x10(11) eV(-1) cm(-2) and 5.8x10(-23), 8.11x10(-23) cm(2) for the NMOS and PMOS structures, respectively. A low value of interface state density in both P-and N-MOS structures makes it a suitable alternate dielectric layer for CMOS applications. And also very low value of capture cross section for both the carriers due to the amphoteric nature of defect indicates that the traps are not aggressive recombination centers and possibly can not contribute to the device operation to a large extent. (C) 2015 Author(s).
Item Type: | Journal Article |
---|---|
Publication: | AIP ADVANCES |
Publisher: | AMER INST PHYSICS |
Additional Information: | Copy right for this article belongs to the AMER INST PHYSICS, 1305 WALT WHITMAN RD, STE 300, MELVILLE, NY 11747-4501 USA |
Department/Centre: | Division of Physical & Mathematical Sciences > Physics |
Date Deposited: | 06 Jan 2016 06:20 |
Last Modified: | 06 Jan 2016 06:20 |
URI: | http://eprints.iisc.ac.in/id/eprint/53051 |
Actions (login required)
View Item |