Quaternary, layered, 2D chalcogenide, Mo1�xWxSSe: thickness dependent transport properties

Kumar, R and Jenjeti, RN and Vankayala, K and Sampath, S (2024) Quaternary, layered, 2D chalcogenide, Mo1�xWxSSe: thickness dependent transport properties. In: Nanotechnology, 35 (4).

PDF nanotechnology_35_2024.pdf - Published Version Restricted to Registered users only Download (1MB) | Request a copy

Abstract

Highly oriented, single crystalline, quaternary alloy chalcogenide crystal, MoxW1�xS2ySe2(1�y), is synthesized using a high temperature chemical vapor transport technique and its transport properties studied over a wide temperature range. Field effect transistors (FET) with bottom gated configuration are fabricated using Mo0.5W0.5SSe flakes of different thicknesses, from a single layer to bulk. The FET characteristics are thickness tunable, with thin flakes (1-4 layers) exhibiting n-type transport behaviour while ambipolar transfer characteristics are observed for thicker flakes (>90 layers). Ambipolar behavior with the dominance of n-type over p-type transport is noted for devices fabricated with layers between 9 and 90. The devices with flake thickness �9 layers exhibit a maximum electron mobility 63 ± 4 cm2 V�1s�1 and an I ON/I OFF ratio >108. A maximum hole mobility 10.3 ± 0.4 cm2 V�1s�1 is observed for the devices with flake thickness �94 layers with I ON/I OFF ratio >102-103 observed for the hole conduction. A maximum I ON/I OFF for hole conduction, 104 is obtained for the devices fabricated with flakes of thickness �7-19 layers. The electron Schottky barrier height values are determined to be �23.3 meV and �74 meV for 2 layer and 94 layers flakes respectively, as measured using low temperature measurements. This indicates that an increase in hole current with thickness is likely to be due to lowering of the band gap as a function of thickness. Furthermore, the contact resistance (R ct) is evaluated using transmission line model (TLM) and is found to be 14 kohm.μm. These results suggest that quaternary alloys of Mo0.5W0.5SSe are potential candidates for various electronic/optoelectronic devices where properties and performance can be tuned within a single composition. © 2023 IOP Publishing Ltd.

Item Type:	Journal Article
Publication:	Nanotechnology
Publisher:	Institute of Physics
Additional Information:	The copyright for this article belongs to Institute of Physics Publishing Ltd.
Keywords:	Chalcogenides; Energy gap; Field effect transistors; Hole mobility; Schottky barrier diodes; Temperature measurement; Transport properties, Chalcogenide crystals; Chemical Vapour Transport; Field-effect transistor; Highest temperature; Hole conduction; Quaternary alloys; Single layer; Single-crystalline; Synthesised; Vapor-transport techniques, Temperature
Department/Centre:	Division of Chemical Sciences > Inorganic & Physical Chemistry
Date Deposited:	23 Jan 2024 05:22
Last Modified:	23 Jan 2024 05:22
URI:	https://eprints.iisc.ac.in/id/eprint/83608

Actions (login required)

View Item