Rapid annealing: minutes to enhance the green emission of the Tb3+-doped ZnGa2O4 nanophosphor with restricted grain growth

Hebbar N, D and Choudhari, KS and Pathak, N and Shivashankar, SA and Kulkarni, SD (2022) Rapid annealing: minutes to enhance the green emission of the Tb3+-doped ZnGa2O4 nanophosphor with restricted grain growth. In: New Journal of Chemistry, 46 (15). pp. 7032-7042.

PDF new_jou_che_46-15_7032-7042_2022 .pdf - Published Version Restricted to Registered users only Download (7MB) | Request a copy

Abstract

The microwave-assisted solvothermal technique (MAST) enabled the synthesis of an ultrafine nanocrystalline green-emitting Tb3+-doped ZnGa2O4 phosphor within minutes. Rapid annealing (RA) of these particles for a mere 15 min facilitated a dramatic increase in the emission intensity without grain growth. Their observed green emission corresponded to standard monochromatic primary green, which, combined with the small particle size (�7 nm), points to their suitability for display applications. We show that the changes during RA are caused mainly during the rapid temperature excursion to the set temperature, followed by 10 min of soaking. Extended soaking or cyclic annealing improved the emission intensity. When the set temperature was 900 °C, the green emission (�545 nm) was enhanced �50-fold, with the CIE coordinates moving towards green, while retaining a particle size of �7-9 nm. The lifetime measurements showed that the dopant exhibits two different coordination environments. Upon RA, their proportions could be tuned, leading to the observed intense green emission and an increase in the overall lifetime. Our work demonstrates a technologically viable technique for producing ZnGa2�xTbxO4 - an ultrafine phosphor suitable for high-resolution display applications. © 2022 The Royal Society of Chemistry

Item Type:	Journal Article
Publication:	New Journal of Chemistry
Publisher:	Royal Society of Chemistry
Additional Information:	The copyright for this article belongs to Royal Society of Chemistry
Keywords:	Annealing; Gallium compounds; Grain growth; Light emission; Nanocrystals; Particle size; Phosphors; Terbium compounds, Display application; Emissions intensity; Green emissions; Microwave-assisted; Nanocrystallines; Nanophosphors; Rapid annealing; Solvothermal techniques; Ultra-fines; Ultrafine, Zinc compounds
Department/Centre:	Division of Interdisciplinary Sciences > Centre for Nano Science and Engineering
Date Deposited:	19 May 2022 05:42
Last Modified:	19 May 2022 05:42
URI:	https://eprints.iisc.ac.in/id/eprint/72024