Vaish, Rahul and Varma, KBR (2008) Crystallisation kinetics of SrLiB9O15 glasses by differential thermal analysis. In: Physics and Chemistry of Glasses - European Journal of Glass Science and Technology Part B, 49 (6). pp. 334-338.
Full text not available from this repository. (Request a copy)Abstract
Transparent glasses of SrLiB9O15 (SLBO) were fabricated via the conventional melt-quenching technique. X-ray powder diffraction (XRD) along with differential thermal analysis (DTA) carried out on the as-quenched samples confirmed their amorphous and glassy nature, respectively. DTA runs were made at different heating rates in order to evaluate the activation energies associated with the glass transition and crystallisation of SrLiB9O15 glasses. The average values of the activation energies for the glass transition and crystallisation of these glasses were 860±10 kJ/mol and 458±10 kJ/mol, respectively. The value of the Avrami exponent n, was 2±0·2 suggesting the process to be one dimensional volume crystallisation. The values of the kinetic parameters that were obtained by different non-isothermal techniques were in close agreement.
Item Type: | Journal Article |
---|---|
Publication: | Physics and Chemistry of Glasses - European Journal of Glass Science and Technology Part B |
Publisher: | Society of Glass Technology |
Additional Information: | Copyright of this article belongs to Society of Glass Technology. |
Department/Centre: | Division of Chemical Sciences > Materials Research Centre |
Date Deposited: | 17 Aug 2009 09:58 |
Last Modified: | 17 Aug 2009 09:58 |
URI: | http://eprints.iisc.ac.in/id/eprint/18591 |
Actions (login required)
![]() |
View Item |