Rao, Ramesh N and Rabinal, MK and Sangunni, KS and Gopal, ESR (1996) Devitrified phases in CuAsSe glasses. In: Physica B, 225 (3-4). pp. 274-282.
![]() |
PDF
Devitrified_phases_in_CuAsSe_glasses.pdf Restricted to Registered users only Download (602kB) | Request a copy |
Abstract
Thermal crystallisation studies of $(Cu_2Se)_x (As_2Se_3)_ {1 -x}$ glasses, where $0.12\leq x \leq 0.5$ (Cu at % of 5 to 25) is carried out using a differential scanning calorimeter (DSC). On heating, glasses with 5 and 10 at% of Cu show a single glass transition temperature and a single crystallisation temperature with a small shoulder. Glasses with Cu content of 15, 20 and 25 at% exhibit the phenomenon of double glass transition and double crystallisation. Isothermal annealing of the glasses at their respective crystallisation temperature(s) results in phase separation. The $Cu3AsSe_2$ compound is the primary crystallisation phase in all the glasses. The thermodynamically stable $Cu3AsSe_4$ compound is an additional primary crystallisation phase in the glasses with 15, 20 and 25 at% of Cu. The monoclinic $As_2Se_3$ compound is the secondary crystallisation product in all the glasses investigated. The presence of these crystalline phases in the devitrified glasses is supported by the multiple melting endotherms observed in the DSC thermograms. An attempt is made to correlate the experimental results with the formal valence shell model.
Item Type: | Journal Article |
---|---|
Publication: | Physica B |
Publisher: | Elsevier |
Additional Information: | Copyright of this article belongs to Elsevier. |
Department/Centre: | Division of Physical & Mathematical Sciences > Physics |
Date Deposited: | 03 Jan 2007 |
Last Modified: | 19 Sep 2010 04:33 |
URI: | http://eprints.iisc.ac.in/id/eprint/9192 |
Actions (login required)
![]() |
View Item |