Nayak, M and Kutty, TRN (1996) Large Range of Nonstoichiometry in Barium Ortho Aluminate Prepared Through Gel-to-Crystallite Conversion. In: Materials Research Bulletin, 31 (2). pp. 227-234.
![]() |
PDF
Large_range_of_nonstoichiometry_in_barium_ortho_aluminate_prepared.pdf Restricted to Registered users only Download (540kB) | Request a copy |
Abstract
Nonstoichiometric barium ortho aluminate with the general formula $Ba_{1-x}Al_2O_{4-x}$ (0 < x < 0.56) was synthesized by the thermal decomposition of barium aluminium oxyhydroxide prepared through gel-to-crystallite conversion method. Phase singularity was confirmed by x-ray powder diffraction. The large range of nonstoichiometry is explained in terms of $Ba^{2+}$ vacancies within the corner sharing $AlO_4$ network, whereby the nepheline structure extends into the stuffed tridymite lattice. HREM studies indicated the ordering of point defects leading to the formation of extended defects and stacking faults. The coordination of aluminium remained tetrahedral as revealed by 27 Al MAS NMR. On doping with Eu(II), $Ba_{1-x-y}Eu_yAl_2O_{4-x+y}$ (0.005 < y < 0.05) shows the emission maximum around 500nm, the intensity of which increases with the x-value
Item Type: | Journal Article |
---|---|
Publication: | Materials Research Bulletin |
Publisher: | Elsevier |
Additional Information: | Copyright of this article belongs to Elsevier. |
Keywords: | A. oxides;C. electron microscopy;C.nuclear magnetic resonance (NMR) D. defects;D. luminescence |
Department/Centre: | Division of Chemical Sciences > Materials Research Centre |
Date Deposited: | 25 Aug 2008 |
Last Modified: | 19 Sep 2010 04:31 |
URI: | http://eprints.iisc.ac.in/id/eprint/8680 |
Actions (login required)
![]() |
View Item |