Kanakaraju, S and Sood, AK and Mohan, S (1998) In situ Raman monitoring of ultrathin Ge films. In: Journal of Applied Physics, 84 (10). pp. 5756-5760.
![]() |
PDF
In_Situ_Raman.pdf Restricted to Registered users only Download (113kB) | Request a copy |
Abstract
We report the in situ interference enhanced Raman spectroscopy of ultrathin crystalline Ge films grown at $300 ^oC$. The Raman spectra of the films show a peak at $\sim290 cm^{-1}$ attributed to the confined optical phonon and a broadband on the low-frequency side at $\sim254 cm^{-1}$ for 5 and 10 Å thick films. The latter is attributed to disordered surface with large number of dangling bonds. For thicker films, the low-frequency mode appears at $270 cm^{-1}$ assigned to surface optical phonons.
Item Type: | Journal Article |
---|---|
Publication: | Journal of Applied Physics |
Publisher: | American Institute of Physics |
Additional Information: | Copyright of this article belongs to American Institute of Physics. |
Department/Centre: | Division of Physical & Mathematical Sciences > Instrumentation Appiled Physics |
Date Deposited: | 07 Jul 2006 |
Last Modified: | 19 Sep 2010 04:29 |
URI: | http://eprints.iisc.ac.in/id/eprint/7801 |
Actions (login required)
![]() |
View Item |