Gandhi, AS and Jayaram, V (2003) Plastically deforming amorphous $ZrO_2-Al_2O_3$. In: Acta Materialia, 51 (6). pp. 1641-1649.
![]() |
PDF
Plastically_deforming_amorphous.pdf Restricted to Registered users only Download (231kB) | Request a copy |
Abstract
We report for the first time non-viscous, plastic deformation in an amorphous oxide: $ZrO_2-Al_2O_3$. Dense samples of amorphous $ZrO_2-Al_2O_3$ made by hot pressing spray-pyrolysed powder were deformed in uniaxial compression at 600–700°C at strain rates from $6\times10^{-5}\hspace{2mm}s^{-1}\hspace{2mm}to\hspace{2mm}10^{-3}\hspace{2mm}s{-1}$. A transition from elastic to plastic deformation occurred at a critical stress ~360 MPa. The onset of plastic deformation was associated with a drop in the stress by 20–25%. Little influence of strain and strain rate on the flow stress was observed. The non-viscous, plastic deformation is related to the open structure of the amorphous phase as indicated by its low true density.
Item Type: | Journal Article |
---|---|
Publication: | Acta Materialia |
Publisher: | Elsevier |
Additional Information: | Copyright of this article belongs to Elsevier. |
Keywords: | Amorphous oxides;Plastic deformation;Shear bands; Compression test |
Department/Centre: | Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy) |
Date Deposited: | 02 Jun 2006 |
Last Modified: | 19 Sep 2010 04:28 |
URI: | http://eprints.iisc.ac.in/id/eprint/7331 |
Actions (login required)
![]() |
View Item |