Kumar, N and Narayan, B and Singh, A and Kumar, S (2020) Enhanced magneto-capacitance in Sr2+ modified BiFeO3�PbTiO3 solid solutions. In: Materials Chemistry and Physics, 252 .
![]() |
PDF
MAT_CHE_PHY_252_2020.pdf - Published Version Restricted to Registered users only Download (2MB) | Request a copy |
Abstract
Polycrystalline ceramics of 0.7BiFeO3-0.3 Pb(1-x)SrxTiO3 compositions with x = 0, 0.2, 0.4, 0.6, 0.8 and 1.0 were successfully synthesized by solid state reaction method. The structural, microstructural, ferroelectric, magnetic, dielectric and magnetocapacitive properties have been investigated. X-Ray diffraction analysis using Rietveld refinement revealed the existence of multiphase region with rhombohedral (R3c) and tetragonal (P4mm) polymorphs for x = 0, 0.2, 0.4, 0.6 & 0.8 and single phase with cubic crystallinity for x = 1.0 with Pm3�m space group. SEM micrographs depicted dense microstructure with non-uniform grains. Except x = 0, pinched ferroelectric loops have been observed for x = 0.2, 0.4, 0.6, 0.8 and 1.0 with low remnant polarization. Sr2+ substitution enhanced the magnetization by suppressing antiferromagnetic spin cycloid of BiFeO3 and the maximum value of remnant was found to be 9.98 memu/g for x = 1.0. Room temperature dielectric studies revealed that the dielectric constant decreases with increasing Sr2+ content in the composition. The magnetoelectric coupling was measured through observing the relative change in dielectric constant induced by applied magnetic field (Magnetocapacitance: MC). The maximum value of magnetocapacitance was found to be 0.88 for the composition with x = 0.6. The magnetic field induced fractional dielectric constant can also be expressed as MC ~ γM2 using Ginzburg�Landau theory and the linear fitting gave the value of positive value of magnetoelectric interaction constant, γ = 3.79, 2.08 and 1.76 for x = 0, 0.06 and 1.0, respectively. © 2020 Elsevier B.V.
Item Type: | Journal Article |
---|---|
Publication: | Materials Chemistry and Physics |
Publisher: | Elsevier Ltd |
Additional Information: | Copy right for this article belongs to Elsevier Ltd |
Keywords: | Crystallinity; Ferroelectricity; Iron compounds; Lead titanate; Magnetic fields; Rietveld refinement; Solid state reactions; X ray powder diffraction, Antiferromagnetic spins; Applied magnetic fields; Dielectric studies; Magnetocapacitance; Magnetoelectric couplings; Polycrystalline ceramics; Remnant polarizations; Solid state reaction method, Bismuth compounds |
Department/Centre: | Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy) |
Date Deposited: | 10 Nov 2020 09:35 |
Last Modified: | 10 Nov 2020 09:35 |
URI: | http://eprints.iisc.ac.in/id/eprint/65961 |
Actions (login required)
![]() |
View Item |