Sudakar, C and Subbanna, GN and Kutty, TRN (2004) Effect of cationic substituents on particle morphology of goethite and the magnetic properties of maghemite derived from substituted goethite. In: Journal of Materials Science, 39 (13). pp. 4271-4286.
Full text not available from this repository. (Request a copy)Abstract
Preparation of nanoparticles with the desired shape and size by the wet-chemical precipitation process is a challenging task. Thus, the effects of different substitutional impurities such as Al, Cr, Co or Ni on the particle morphology and phase stability of goethite have been investigated. Goethite is prepared by air oxidation of $Fe(OH)_2 · xH_2O$ gel under near neutral conditions. Below certain concentration levels of dopants $(Al^{3+} \leq 10; Cr^{3+} \leq 5; Co^{2+} \leq 10$ and $Ni^{2+} \leq 5 at.%)$ the samples remained monophasic as revealed by XRD, TEM, and IR studies. Above these levels, the substituents produce traces of secondary phases such as lepidocrocite, spinel ferrite and $M^n(OH)_n$. The goethite structure is stable in spite of the iso- or aliovalent substitutions. The individual additives have divergent influence on the particle morphology; $Al^{3+}$ and $Cr^{3+}$ decreases the particle size to <50 nm and aspect ratio (AR) <2. Co-substitution produces slender particles with AR as high as 25. Whereas, $Ni^{2+}$ does not have any influence on the particle morphology. The attributable factors in morphology control are the increased nucleation rate, restricted growth along needle axes, and the strain induced in the goethite lattice as a result of difference in ionic radii. Maghemite, $\gamma -Fe_2O_3– \delta$, particles are obtained from goethite wherein the topotactic conversion renders the retention of the particle morphology of the precursor. Maghemite with substituted impurities showed substantial differences in magnetic properties. Saturation magnetization $(\sigma s)$ and coercivity $(H_ c)$ go down to very low values due to relaxation of spins on the surface atoms as revealed by Mössbauer spectroscopy. Decrease in coercivity is by way of the presence of diamagnetic ion $(Al^{3+})$. Whereas, Co-substituted maghemite has enhanced $H_ c$ as a result of high magnetocrystalline anisotropy accompanied by the shape anisotropy.
Item Type: | Journal Article |
---|---|
Publication: | Journal of Materials Science |
Publisher: | Springer |
Additional Information: | The copyright belongs to Springer. |
Department/Centre: | Division of Chemical Sciences > Materials Research Centre |
Date Deposited: | 25 Apr 2006 |
Last Modified: | 27 Aug 2008 11:55 |
URI: | http://eprints.iisc.ac.in/id/eprint/6467 |
Actions (login required)
![]() |
View Item |