Chetty, Raju and Bali, Ashoka and Mallik, Ramesh Chandra (2016) Thermoelectric properties of indium doped Cu2CdSnSe4. In: INTERMETALLICS, 72 . pp. 17-24.
![]() |
PDF
Int_72_17_2016.pdf - Published Version Restricted to Registered users only Download (2MB) | Request a copy |
Abstract
Recently, research in copper-based quaternary chalcogenide materials has been found to be interesting for the study of thermoelectric properties because of their low thermal conductivity due to complex crystal structures. In the present work, stoichiometric quaternary chalcogenide compounds Cu2CdSn1-xInxSe4(x = 0, 0.025, 0.05, 0.1) were prepared by solid state synthesis. The powder X-ray diffraction patterns of all the samples showed a tetragonal crystal structure with the space group I (4) over bar 2m of the main phase. In addition to this phase, a small amount of impurity phase CdSe was present in all the samples, as confirmed by Rietveld analysis. The elemental composition of all the samples characterized by an Electron Probe Micro Analyzer showed a slight deviation from the nominal composition. The transport properties were measured in the temperature range of 350 K-723 K. The positive Seebeck coefficient of all the compounds indicate that the majority carriers are holes. The Seebeck coefficient and electrical resistivity did not follow the trend in the expected manner with In doping, which could be influenced by the presence of the impurity phases. The total thermal conductivity of all the samples was dominated by the lattice thermal conductivity, while the electronic contribution was very small due to the low carrier contribution. A lattice thermal conductivity decrease with an increase of temperature indicates the dominance of phonon-phonon scattering at higher temperatures. The maximum figure of merit zT = 0.30 at 723 K was obtained for the compound Cu2CdSn0.9In0.1Se4. (C) 2016 Elsevier Ltd. All rights reserved.
Item Type: | Journal Article |
---|---|
Publication: | INTERMETALLICS |
Publisher: | ELSEVIER SCI LTD |
Additional Information: | Copy right for this article belongs to the ELSEVIER SCI LTD, THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, OXON, ENGLAND |
Keywords: | Electrical properties; Thermoelectric properties; Powder metallurgy; Diffraction (X-ray); Electron microscopy; Scanning |
Department/Centre: | Division of Physical & Mathematical Sciences > Physics |
Date Deposited: | 23 Apr 2016 05:10 |
Last Modified: | 23 Apr 2016 05:10 |
URI: | http://eprints.iisc.ac.in/id/eprint/53671 |
Actions (login required)
![]() |
View Item |