Outstanding dielectric constant and piezoelectric coefficient in electrospun nanofiber mats of PVDF containing silver decorated multiwall carbon nanotubes: assessing through piezoresponse force microscopy

Sharma, Maya and Srinivas, Vijay and Madras, Giridhar and Bose, Suryasarathi (2016) Outstanding dielectric constant and piezoelectric coefficient in electrospun nanofiber mats of PVDF containing silver decorated multiwall carbon nanotubes: assessing through piezoresponse force microscopy. In: RSC ADVANCES, 6 (8). pp. 6251-6258.

PDF RSC_Adv_6-8_6251_2016.pdf - Published Version Restricted to Registered users only Download (1MB) | Request a copy

Abstract

In order to enhance the piezoelectric b-phase, PVDF was electrospun from DMF solution. The enhanced b-phase was discerned by comparing the electrospun fibers against the melt mixed samples. While both the processes resulted in phase transformation of a-to electroactive b-polymorph in PVDF, the fraction of b-phase was strongly dependent on the adopted process. Two different nanoscopic particles: carboxyl functionalized multiwall carbon nanotubes (CNTs) and silver (Ag) decorated CNTs were used to further enhance the piezoelectric coefficient in the electrospun fibers. Fourier transform infrared spectroscopy (FTIR) and wide-angle X-ray diffraction (XRD) supports the development of piezoelectric b-phase in PVDF. It was concluded that electrospinning was the best technique for inducing the b-polymorph in PVDF. This was attributed to the high voltage electrostatic field that generates extensional forces on the polymer chains that aligns the dipoles in one direction. The ferroelectric and piezoelectric measurement on electrospun fibers were studied using piezo-response force microscope (PFM). The Ag-CNTs filled PVDF electrospun fibers showed the highest piezoelectric coefficient (d(33) = 54 pm V-1) in contrast to PVDF/CNT fibers (35 pm V-1) and neat PVDF (30 pm V-1). This study demonstrates that the piezoelectric coefficient can be enhanced significantly by electrospinning PVDF containing Ag decorated nanoparticles.

Item Type:	Journal Article
Publication:	RSC ADVANCES
Publisher:	ROYAL SOC CHEMISTRY
Additional Information:	Copy right for this article belongs to the ROYAL SOC CHEMISTRY, THOMAS GRAHAM HOUSE, SCIENCE PARK, MILTON RD, CAMBRIDGE CB4 0WF, CAMBS, ENGLAND
Department/Centre:	Division of Mechanical Sciences > Chemical Engineering Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy) Division of Interdisciplinary Sciences > Centre for Nano Science and Engineering
Date Deposited:	04 Mar 2016 07:41
Last Modified:	04 Mar 2016 07:41
URI:	http://eprints.iisc.ac.in/id/eprint/53328

Actions (login required)

View Item