Electromagnetic shielding materials and coatings derived from gelation of multiwall carbon nanotubes in an LCST mixture

Xavier, Priti and Bose, Suryasarathi (2014) Electromagnetic shielding materials and coatings derived from gelation of multiwall carbon nanotubes in an LCST mixture. In: RSC ADVANCES, 4 (98). pp. 55341-55348.

PDF rsc_adv_4-98_55341_2014.pdf - Published Version Restricted to Registered users only Download (953kB) | Request a copy

Abstract

Thermally induced demixing in an LCST mixture, polystyrene (PS)/polyvinyl methyl ether] (PVME), was used as a template to design materials with high electrical conductivity. This was facilitated by gelation of multiwall carbon nanotubes (MWNTs) in a given phase of the blends. The MWNTs were mixed in the miscible blends and the thermodynamic driven demixing further resulted in selective localization in the PVME phase of the blends. This was further confirmed by atomic force microscopy (AFM). The time dependent gelation of MWNTs at shallow quench depth, evaluated using isochronal temperature sweep by rheology, was studied by monitoring the melt electrical conductivity of the samples in situ by an LCR meter coupled to a rheometer. By varying the composition in the mixture, several intricate shapes like gaskets and also coatings capable of attenuating the EM radiation in the microwave frequency can be derived. For instance, the PVME rich mixtures can be molded in the form of a gasket, O-ring and other intricate shapes while the PS rich mixtures can be coated onto an insulating polymer to enhance the shielding effectiveness (SE) for EM radiation. The SE of the various materials was analyzed using a vector network analyzer in both the X-band (8.2 to 12 GHz) and the K-u-band (12 to 18 GHz) frequency. The improved SE upon gelation of MWNTs in the demixed blends is well evident by comparing the SE before and after demixing. A reflection loss of -35 dB was observed in the blends with 2 wt% MWNTs. Further, by coating a layer of ca. 0.15 mm of PS/PVME/MWNT, a SE of -15 dB at 18 GHz could be obtained.

Item Type:	Journal Article
Publication:	RSC ADVANCES
Publisher:	ROYAL SOC CHEMISTRY
Additional Information:	Copyright for this article belongs to the ROYAL SOC CHEMISTRY, THOMAS GRAHAM HOUSE, SCIENCE PARK, MILTON RD, CAMBRIDGE CB4 0WF, CAMBS, ENGLAND
Department/Centre:	Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited:	29 Dec 2014 05:47
Last Modified:	29 Dec 2014 05:47
URI:	http://eprints.iisc.ac.in/id/eprint/50549

Actions (login required)

View Item