Dar, Ibrahim M and Sampath, S and Shivashankar, SA (2014) Exploiting oriented attachment in stabilizing La3+-doped gallium oxide nano-spindles. In: RSC ADVANCES, 4 (90). pp. 49360-49366.
![]() |
PDF
rsc_adv_4-90_49360_2014.pdf - Published Version Restricted to Registered users only Download (2MB) | Request a copy |
Abstract
Retaining the morphology of gallium oxide nanostructures during structural transformations or after doping with lanthanide ions is not facile. Here we report on the sonochemical synthesis of nearly monodisperse similar to 550 nm long nano-spindles of undoped and La-doped alpha-GaOOH. The transformation of as-prepared undoped and La-doped alpha-GaOOH powders into the corresponding undoped and La-doped Ga2O3 phases (alpha and beta) was achieved by carrying out controlled annealing at elevated temperatures under optimized conditions. The formation of gallium oxide nano-spindles is explained by invoking the phenomenon of oriented attachment, as amply supported by electron microscopy. Interestingly, the morphology of the gallium oxide nano-spindles remained conserved even after doping them with more than 1.4 at% of La3+ ions. Such robust structural stability could be attributed to the oriented attachment-type growth observed in the nano-spindles. The as-prepared samples and the corresponding annealed ones were thoroughly characterized by powder X-ray diffraction (PXRD), electron microscopy (SEM, TEM, and STEM-EDS) and X-ray photoelectron spectroscopy (XPS). Finally, photoluminescence from the single-crystalline undoped and La-doped beta-Ga2O3 was explored.
Item Type: | Journal Article |
---|---|
Publication: | RSC ADVANCES |
Publisher: | ROYAL SOC CHEMISTRY |
Additional Information: | Copy right for this article belongs to the ROYAL SOC CHEMISTRY, THOMAS GRAHAM HOUSE, SCIENCE PARK, MILTON RD, CAMBRIDGE CB4 0WF, CAMBS, ENGLAND |
Department/Centre: | Division of Chemical Sciences > Inorganic & Physical Chemistry Division of Chemical Sciences > Materials Research Centre Division of Interdisciplinary Sciences > Centre for Nano Science and Engineering |
Date Deposited: | 04 Dec 2014 04:50 |
Last Modified: | 04 Dec 2014 04:50 |
URI: | http://eprints.iisc.ac.in/id/eprint/50378 |