Temperature dependent electrical behaviour of Cu2SnS3 films

Dias, Sandra and Krupanidhi, SB (2014) Temperature dependent electrical behaviour of Cu2SnS3 films. In: AIP ADVANCES, 4 (3).

PDF aip_adv_4-3_2014.pdf - Published Version Restricted to Registered users only Download (1MB) | Request a copy

Abstract

The temperature dependent electrical properties of the dropcasted Cu2SnS3 films have been measured in the temperature range 140 K to 317 K. The log I versus root V plot shows two regions. The region at lower bias is due to electrode limited Schottky emission and the higher bias region is due to bulk limited Poole Frenkel emission. The ideality factor is calculated from the ln I versus V plot for different temperatures fitted with the thermionic emission model and is found to vary from 6.05 eV to 12.23 eV. This large value is attributed to the presence of defects or amorphous layer at the Ag / Cu2SnS3 interface. From the Richardson's plot the Richardson's constant and the barrier height were calculated. Owing to the inhomogeneity in the barrier heights, the Richardson's constant and the barrier height were also calculated from the modified Richardson's plot. The I-V-T curves were also fitted using the thermionic field emission model. The barrier heights were found to be higher than those calculated using thermionic emission model. From the fit of the I-V-T curves to the field emission model, field emission was seen to dominate in the low temperature range of 140 K to 177 K. The temperature dependent current graphs show two regions of different mechanisms. The log I versus 1000/T plot gives activation energies E-a1 = 0.367095 - 0.257682 eV and E-a2 = 0.038416 - 0.042452 eV. The log ( I/T-2) versus 1000/T graph gives trap depths Phi(o1) = 0.314159 - 0.204752 eV and Phi(o2) = 0.007425- 0.011163 eV. With increasing voltage the activation energy E-a1 and the trap depth Phi(o1) decrease. From the ln (IT1/ 2) versus 1/T-1/ 4 graph, the low temperature region is due to variable range hopping mechanism and the high temperature region is due to thermionic emission. (C) 2014 Author(s).

Item Type:	Journal Article
Publication:	AIP ADVANCES
Publisher:	AMER INST PHYSICS
Additional Information:	Copyright for this article belongs to the AMER INST PHYSICS, USA
Department/Centre:	Division of Chemical Sciences > Materials Research Centre
Date Deposited:	20 May 2014 05:13
Last Modified:	20 May 2014 05:13
URI:	http://eprints.iisc.ac.in/id/eprint/49103

Actions (login required)

View Item