Praveena, K and Srinath, S (2013) The effect of Sb on the electrical and magnetic properties of Ni-Zn ferrites prepared by sol-gel autocombustion method. In: JOURNAL OF ELECTROCERAMICS, 31 (1-2). pp. 168-175.
![]() |
PDF
Jou_Ele_Cer_31,1-2_168_2013.pdf - Published Version Restricted to Registered users only Download (556kB) | Request a copy |
Abstract
Polycrystalline Ni-Zn ferrites with a well-defined composition of Ni0.4Zn0.6Fe2-xSbxO4 synthesized using sol-gel method. Morphological characterizations on the prepared samples were performed by high resolution transmission electron and field emission scanning electron microscopy. The powders were densified using microwave sintering method. The room temperature complex permittivity (epsilon' and epsilon aEuro(3)) and permeability (mu' and mu aEuro(3)) were measured over a wide frequency range from 1 MHz-1.8 GHz. The real part of permittivity varies as `x' concentration increases and the resonance frequency was observed at much higher frequencies and there is a significant decrease in the loss factor (tan delta). The electrical resistivity and permeability of NiZn ferrites increased with an increase of Sb content. As the concentration of `x' increases from 0 to 0.08 the saturation magnetisation decreases. The saturation magnetization (M-s) a parts per thousand aEuro parts per thousand 52.211 A.m(2)/Kg for x = 0 at room temperature. The room temperature electro paramagnetic resonance (EPR) were studied.
Item Type: | Journal Article |
---|---|
Publication: | JOURNAL OF ELECTROCERAMICS |
Publisher: | SPRINGER |
Additional Information: | copyright for this article belongs to SPRINGER |
Keywords: | Ferrites; Microwave sintering; Electrical resistivity; Dielectric constant; Magnetic properties; EPR |
Department/Centre: | Division of Chemical Sciences > Materials Research Centre |
Date Deposited: | 13 Nov 2013 10:53 |
Last Modified: | 13 Nov 2013 10:53 |
URI: | http://eprints.iisc.ac.in/id/eprint/47749 |
Actions (login required)
![]() |
View Item |