Preparation and characterization chemistry of nano-crystalline Ni-Cu-Zn ferrite

Hashim, Mohd and Alimuddin, * and Shirsath, Sagar E and Kumar, Shalendra and Kumar, Ravi and Roy, Aashis S and Shah, Jyoti and Kotnala, RK (2013) Preparation and characterization chemistry of nano-crystalline Ni-Cu-Zn ferrite. In: JOURNAL OF ALLOYS AND COMPOUNDS, 549 . pp. 348-357.

PDF jol_all_com_549_348_2013.pdf - Published Version Restricted to Registered users only Download (1MB) | Request a copy

Abstract

In submitted research; nanocrystalline powders having elements Ni0.5Cu0.25Zn0.25Fe2 xInxO4 with varied amounts of indium ( x = 0.0, 0.1, 0.2, 0.3 and 0.4) were grown-up by modified citrate to nitrate alchemy. The realism of single phase cubic spinel creation of the synthesized ferrite samples was studied by the DTA-TGA, XRD, SEM, EDX, FT-IR, VSM and dielectric measurements. SEM was applied to inspect the morphological variations and EDX was used to determine the compositional mass ratios. The studies on the dielectric constant (epsilon'), dielectric loss (epsilon `'), loss tangent (tan delta), ac conductivity (sigma(ac)), resistive and reactive parts of the impedance analysis (Z' and Z `') at room temperature were also carried out. The saturation magnetizations (Ms) were determined using the vibrating sample magnetometer (VSM). Ms. decreased with the increase In3+ doping content, as Fe3+ of 5(mu B) ions are replaced by In3+ of 5 mu(B) ions. (C) 2012 Elsevier B. V. All rights reserved.

Item Type:	Journal Article
Publication:	JOURNAL OF ALLOYS AND COMPOUNDS
Publisher:	ELSEVIER SCIENCE SA
Additional Information:	Copyright for this article belongs to ELSEVIER SCIENCE SA, SWITZERLAND
Keywords:	Ni-Cu-Zn ferrites;Nanoparticles;Sol-gel chemistry;TG-DTA;Magnetization
Department/Centre:	Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited:	24 Jan 2013 05:15
Last Modified:	24 Jan 2013 05:15
URI:	http://eprints.iisc.ac.in/id/eprint/45629

Actions (login required)

View Item