Jena, Anirudha and Munichandraiah, N and Shivashankar, SA (2012) Morphology Controlled Growth of Meso-Porous Co3O4 Nanostructures and Study of Their Electrochemical Capacitive Behavior. In: JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 159 (10). A1682-A1689.
![]() |
PDF
Jol_Ele_Soc_159-10_A1682_2012.pdf - Published Version Restricted to Registered users only Download (1MB) | Request a copy |
Abstract
The morphology of nanocrystalline Co3O4 synthesized through microwave irradiation of a solution of a cobalt complex is found to depend reproducibly on the conditions of synthesis and, in particular, on the composition of the solvent used. Despite the rapidity of the process, oriented aggregation occurs under certain conditions, depending on solvent composition. Annealing the oriented samples leads to microstructures with significant porosity, rendering the material suitable as electrodes for electrochemical capacitors. Electrochemical analysis of the oxide samples was carried out in 0.1M Na2SO4 electrolyte vs. Ag/AgCl electrode. A stable specific capacitance of 221 F/g was measured for a meso-porous sample displaying oriented aggregation. Stability of these oxide materials were checked for longer charge-discharge cycling. (C) 2012 The Electrochemical Society. DOI: 10.1149/2.002210jes] All rights reserved.
Item Type: | Journal Article |
---|---|
Publication: | JOURNAL OF THE ELECTROCHEMICAL SOCIETY |
Publisher: | ELECTROCHEMICAL SOC INC |
Additional Information: | Copyright for this article belongs to ELECTROCHEMICAL SOC INC, USA |
Department/Centre: | Division of Chemical Sciences > Inorganic & Physical Chemistry Division of Chemical Sciences > Materials Research Centre Division of Interdisciplinary Sciences > Centre for Nano Science and Engineering |
Date Deposited: | 07 Dec 2012 08:32 |
Last Modified: | 07 Dec 2012 08:32 |
URI: | http://eprints.iisc.ac.in/id/eprint/45526 |
Actions (login required)
![]() |
View Item |