Preetha, P and Thomas, MJ (2010) AC breakdown characteristics of epoxy alumina nanocomposites. In: 2010 Annual Report Conference on Electrical Insulation and Dielectric Phenomena (CEIDP), 17-20 Oct. 2010, West Lafayette, IN.
![]() |
PDF
AC_breakdown.pdf - Published Version Restricted to Registered users only Download (594kB) | Request a copy |
Abstract
Experiments were conducted to measure the ac breakdown strength of 0.5 mm, thick epoxy alumina nanocomposites with different filler concentrations of 0.1, 1 and 5wt%. The experiments were performed as per the ASTM D 149 standard. It was observed that the ac breakdown strength was marginally lower up to 1wt% filler concentration and then increased at 5wt% filler concentration as compared to the unfilled epoxy. The Weibull shape parameter (β) increased with the addition of nanoparticles to epoxy. The dependence of thickness on the ac breakdown strength was also analyzed by conducting experiments on 1mm and 3mm thick unfilled epoxy and epoxy alumina nanocomposites of 1wt% and 5wt% filler concentrations. The DSC analysis was done to understand the material properties at the filler resin interface in order to study the effect of the filler concentration and thereby the influence of the interface on the ac breakdown strength of epoxy nanocomposites.
Item Type: | Conference Paper |
---|---|
Publisher: | IEEE |
Additional Information: | Copyright 2010 IEEE. Personal use of this material is permitted.However, permission to reprint/republish this material for advertising or promotional purposes or for creating new collective works for resale or redistribution to servers or lists, or to reuse any copyrighted component of this work in other works must be obtained from the IEEE. |
Department/Centre: | Division of Electrical Sciences > Electrical Engineering |
Date Deposited: | 20 Dec 2011 06:26 |
Last Modified: | 20 Dec 2011 06:26 |
URI: | http://eprints.iisc.ac.in/id/eprint/39072 |
Actions (login required)
![]() |
View Item |