Jacob, KT and Ranjani, R (2011) Thermodynamic properties of LaFeO3-delta and LaFe12O19. In: Materials Science and Engineering B, 176 (7). pp. 559-566.
![]() |
PDF
Thermodynamic.pdf - Published Version Restricted to Registered users only Download (711kB) | Request a copy |
Abstract
The standard Gibbs energies of formation of lanthanum orthoferrite (LaFeO3-delta) and hexaferrite (LaFe12O19)were determined using solid-state electrochemical cells incorporating yttria-stabilized zirconia as the electrolyte and pure oxygen gas at ambient pressure as the reference electrode. From emf of the solid-state cell, the Gibbs energy of formation of nonstoichiometric orthoferrite (LaFeO3-delta) is obtained. To derive values for the stoichiometric phase, variation of the oxygen nonstoichiometric parameter with oxygen partial pressure was measured using thermogravimetry under controlled gas mixtures. The results obtained for LaFeO3 and LaFe12O19 can be summarized by the following equations, which represent the formation of ternary oxides from their component binary oxides: 1/2 La2O3 + 1/2 Fe2O3 -> LaFeO3: Delta G degrees (LaFeO3) (+/- 450) (J mol(-1)) = -62920 - 2.12T (K), and 1/2 La2O3 + 9/2Fe(2)O(3) + Fe3O4 -> LaFe12O19; Delta G degrees (LaFe12O19) (+/- 200) (J mol(-1)) = -103900 + 21.25T (K). These data are discussed critically in comparison with thermodynamic values reported in the literature from a variety of measurements. The values obtained in this study are consistent with calorimetric entropy and enthalpy of formation of the perovskite phase and with some of the Gibbs energy measurements reported in the literature. For the lanthanum hexaferrite (LaFe12O19) there are no prior thermodynamic measurements for comparison. (c) 2011 Elsevier B.V. All rights reserved.
Item Type: | Journal Article |
---|---|
Publication: | Materials Science and Engineering B |
Publisher: | Elsevier Science B.V. |
Additional Information: | Copyright of this article belongs to Elsevier Science B.V. |
Keywords: | Oxygen non-stoichiometry;Lanthanum orthoferrite;Lanthanum hexaferrite;Gibbs free energy;Enthalpy;Entropy |
Department/Centre: | Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy) |
Date Deposited: | 09 Jun 2011 05:20 |
Last Modified: | 09 Jun 2011 05:20 |
URI: | http://eprints.iisc.ac.in/id/eprint/38213 |