Thermo and photoluminescence properties of Eu3+ activated hexagonal, monoclinic and cubic gadolinium oxide nanorods

Dhananjaya, N and Nagabhushana, H and Nagabhushana, BM and Rudraswamy, B and Shivakumara, C and Ramesh, KP and Chakradhar, RPS (2011) Thermo and photoluminescence properties of Eu3+ activated hexagonal, monoclinic and cubic gadolinium oxide nanorods. In: Physica B: Condensed Matter, 406 (9). pp. 1645-1652.

PDF Thermo.pdf - Published Version Restricted to Registered users only Download (475kB) | Request a copy

Abstract

Different phases of Eu3+ activated gadolinium oxide (Gd (OH)(3), GdOOH and Gd2O3) nanorods have been prepared by the hydrothermal method with and without cityl trimethyl ammonium bromide (GAB) surfactant. Cubic Gd2O3:Eu (8 mol%) red phosphor has been prepared by the dehydration of corresponding hydroxide Gd(OH)(3):Eu after calcinations at 350 and 600 degrees C for 3 h, respectively. When Eu3+ ions were introduced into Gd(OH)(3), lattice sites which replace the original Gd3+ ions, a strong red emission centered at 613 nm has been observed upon UV illumination, due to the intrinsic Eu3+ transition between D-5(0) and F-7 configurations. Thermoluminescence glow curves of Gd (OH)(3): Eu and Gd2O3:Eu phosphors have been recorded by irradiating with gamma source ((CO)-C-60) in the dose range 10-60 Gy at a heating rate of 6.7 degrees C sec(-1). Well resolved glow peaks in the range 42-45, 67-76,95-103 and 102-125 degrees C were observed. When gamma-irradiation dose increased to 40 Gy, the glow peaks were reduced and with increase in gamma-dose (50 and 60 Gy) results the shift in first two glow peak temperatures at about 20 degrees C and a new shouldered peak at 86 degrees C was observed. It is observed that there is a shift in glow peak temperatures and variation in intensity, which is mainly attributed to different phases of gadolinium oxide. The trapping parameters namely activation energy (E), order of kinetics (b) and frequency factor were calculated using peak shape and the results are discussed. (C) 2010 Elsevier B.V. All rights reserved.

Item Type:	Journal Article
Publication:	Physica B: Condensed Matter
Publisher:	Elsevier Science B.V.
Additional Information:	Copyright of this article belongs to Elsevier Science B.V.
Keywords:	Nanorods;Gadolinium oxide;UV-vis;Photoluminescence; Thermoluminescence
Department/Centre:	Division of Chemical Sciences > Solid State & Structural Chemistry Unit Division of Physical & Mathematical Sciences > Physics
Date Deposited:	01 Jun 2011 11:44
Last Modified:	01 Jun 2011 11:44
URI:	http://eprints.iisc.ac.in/id/eprint/37799

Actions (login required)

View Item