Manikandan, N and Asokan, S (2007) Effect of indium doping on the electrical switching behaviour of Ge-Te glasses. In: Philosophical Magazine, 87 (32). 5109 -5116.
![]() |
PDF
884525_.pdf - Published Version Restricted to Registered users only Download (229kB) | Request a copy |
Abstract
Bulk Ge15Te85-xInx (1 <= x <= 11) series of glasses have been found to exhibit a threshold switching behaviour for an input current of 2 mA. An initial decrease is seen in the switching voltages (V-T) with the addition of indium, which is due to the higher metallicity of indium. An increase is seen in V-T above 3 at.% of indium, which proceeds until 8 at.%, with a change in slope (lower to higher) seen around 7 at.%. Beyond x = 8, a reversal in trend is exhibited in the variation of V-T, with a well-defined minimum around x = 9 at.%. Based on the composition dependence of V-T, it is proposed that Ge15Te85-xInx glasses exhibit an extended rigidity percolation threshold. The composition, x = 3, at which the V-T starts to increase and the composition, x = 7, at which a slope change is exhibited correspond to the onset and completion, respectively, of the extended stiffness transition. Thermal studies and photoconductivity e85-xInx glasses. In addition, the minimum seen in V-T at x = 9 is associated with the chemical threshold (CT) of this glassy system.
Item Type: | Journal Article |
---|---|
Publication: | Philosophical Magazine |
Publisher: | Taylor and Francis Group |
Additional Information: | Copyright of this article belongs to Taylor and Francis Group. |
Department/Centre: | Division of Physical & Mathematical Sciences > Instrumentation Appiled Physics |
Date Deposited: | 10 Jun 2010 09:14 |
Last Modified: | 19 Sep 2010 05:57 |
URI: | http://eprints.iisc.ac.in/id/eprint/26207 |
Actions (login required)
![]() |
View Item |