Yuvaraj, D and Nanda, KK and Rao, K Narasimha (2009) Synthesis of ZnO Nanoneedles on Flexible Polymer Substrates at Room Temperature by Activated Reactive Evaporation. In: Current Nanoscience, 5 (3). pp. 283-288.
Full text not available from this repository. (Request a copy)Abstract
ZnO nanoneedles were successfully deposited on flexible polymer substrates at room temperature by activated reactive evaporation. Neither a catalyst nor a template was employed in this synthesis. These synthesized needles measured 500 - 600 nm in length and its diameter varied from 30 - 15 nm from the base to the tip. The single-crystalline nature of the nanoneedle was observed by high-resolution transmission electron microscopy studies. The Raman studies on these nanoneedles had shown that they are oxygen deficient in nature. A possible growth mechanism has been proposed here, in which the nanoneedles nucleate and grow in the gas phase by vapor-solid mechanism.
Item Type: | Journal Article |
---|---|
Publication: | Current Nanoscience |
Publisher: | Bentham Science Publishers Ltd |
Additional Information: | Copyright for this article belongs to Bentham Science Publishers Ltd. |
Keywords: | Nanoneedle; activated reactive evaporation; ZnO; gas phase; nanostructures on flexible substrates |
Department/Centre: | Division of Chemical Sciences > Materials Research Centre Division of Physical & Mathematical Sciences > Instrumentation Appiled Physics |
Date Deposited: | 02 Dec 2009 05:04 |
Last Modified: | 02 Dec 2009 05:04 |
URI: | http://eprints.iisc.ac.in/id/eprint/24992 |
Actions (login required)
![]() |
View Item |