Magnetic structure of sodium and potassium doped lanthanum manganites

Das, A and Sahana, M and Yusuf, SM and Rao, Madhav L and Shivakumara, C and Hegde, MS (2000) Magnetic structure of sodium and potassium doped lanthanum manganites. In: Materials Research Bulletin, 35 (5). pp. 651-659.

[img] PDF
Restricted to Registered users only

Download (219kB) | Request a copy


Neutron diffraction, depolarization, and magnetization measurements were carried out on Na $(La_{0.82}Na_{0.13}MnO_{2.93})$ and K $(La_{0.82}K_{0.08}MnO_{2.89})$ doped lanthanum manganites. The study shows that both the compounds are ferromagnetic below 300 K. Low-temperature magnetic structure refinement together with the magnetization (M) measurements suggest that both the compounds have a canted ferromagnetic structure at 14 K. Smooth variation of the magnetic peak intensity $(\alpha\hspace{2mm}M^2)$ as a function of temperature could be fitted to the mean field approximation relationship, which indicates that, there is no abrupt change in the canting angle with temperature. Magnetic domain size (which is restricted by the grain size in the polycrystalline samples) obtained from the neutron depolarization measurements was found to be ~1–2 \mu m in a magnetic field of 1.2 kOe for both samples.

Item Type: Journal Article
Publication: Materials Research Bulletin
Publisher: Elsevier
Additional Information: Copyright of this article belongs to Elsevier.
Keywords: A. Magnetic materials;A. Oxides;D. Magnetic structure
Department/Centre: Division of Chemical Sciences > Solid State & Structural Chemistry Unit
Date Deposited: 30 Oct 2006
Last Modified: 19 Sep 2010 04:32
URI: http://eprints.iisc.ac.in/id/eprint/8902

Actions (login required)

View Item View Item