Na substitution for La- and Mn-sites in $LaMnO_3$ from alkali halide fluxes: low temperature synthesis, structure and properties

Shivakumara, C and Subbanna, GN and Lalla, NP and Hegde, MS (2004) Na substitution for La- and Mn-sites in $LaMnO_3$ from alkali halide fluxes: low temperature synthesis, structure and properties. In: Materials Research Bulletin, 39 (1). pp. 71-81.

PDF Na_substitution-635.pdf Restricted to Registered users only Download (415kB) | Request a copy

Abstract

$La_{1-x}Na_xMn_{1-y}Na_yO_3$ (0.12 < x < 0.16;0.04 < y < 0.07) have been synthesized from NaBr and NaI fluxes at relatively low temperature of 850 and $750^o\hspace{2mm}C$, respectively. Final composition of these oxides was obtained from chemical analysis of the elements present. The flux grown oxides crystallize in the rhombohedral structure (space group R-3c, No. 167) and are ferromagnetic metals (FMM). Chemical analysis and Rietveld refinement of X-ray data indicate Na ion is substituted for both La- and Mn-sites in the compound prepared from NaBr and NaI fluxes with 33 and 49% of $Mn^{4+}$ concentration, respectively.

Item Type:	Journal Article
Publication:	Materials Research Bulletin
Publisher:	Elsevier
Additional Information:	The copyright of this article belongs to Elsevier.
Keywords:	A. Oxides;B. Chemical synthesis;C. X-ray diffraction;D. Magnetic properties
Department/Centre:	Division of Chemical Sciences > Materials Research Centre Division of Chemical Sciences > Solid State & Structural Chemistry Unit
Date Deposited:	02 Jun 2006
Last Modified:	19 Sep 2010 04:28
URI:	http://eprints.iisc.ac.in/id/eprint/7371

Actions (login required)

View Item