Influence of mineral admixtures and aggregates on properties of different concretes under high temperature conditions I: Experimental study

Reddy, D Harinadha and Ramaswamy, Ananth (2017) Influence of mineral admixtures and aggregates on properties of different concretes under high temperature conditions I: Experimental study. In: Journal of Building Engineering, 14 . pp. 103-114. ISSN 23527102

PDF jou_bui_eng_14_103-114_2017 .pdf - Published Version Restricted to Registered users only Download (2MB) | Request a copy

Abstract

Fire in concrete structures deteriorates mechanical properties of the material and leads to structural collapse under loads. Two types of spalling occurs in concrete when exposed to high temperature, namely explosive and thermal spalling. Explosive spalling occurs once the hydrostatic stress (developed in the pores) exceeds the tensile strength of the concrete. Where as thermal spalling of concrete happens due to degradation of material properties (elastic modulus, compressive and tensile strength) when exposed to high temperature. The present study comprises of an experimental (this manuscript) and analytical program (part II) to assess deformations due to high temperature in different concretes. Seven different concrete mixes have been made for this purpose and among the seven mixes, three mixes are self compacted concrete mixes (35 MPa, 55 MPa and 70 MPa), a high volume fly ash concrete mix (45 MPa), a normally vibrated OPC concrete mix (45 MPa) and a heavy density concrete mix (25 MPa). Two ages were selected to test these concretes to study the age effects, one at 28 days and other at 365 days. All these mixes were tested in three different test approaches, which are stressed (ST), unstressed (UST) and unstressed residual strength (URST) approach. Each approach has its specific purpose of extracting residual properties of concrete when exposed to high temperature. The findings indicate that both concrete with supplementary cementitious material (fly ash) and heavy density concrete (Haemetite) were gound to be structurally robust when exposed to high temperature. © 2017 Elsevier Ltd

Item Type:	Journal Article
Publication:	Journal of Building Engineering
Publisher:	Elsevier Ltd
Additional Information:	The copyright for this article belongs to the Elsevier Ltd.
Keywords:	Explosive spalling; Fly ash; Heavy density concrete; High temperature; Self compacted concrete; Silica fume
Department/Centre:	Division of Mechanical Sciences > Civil Engineering
Date Deposited:	31 May 2022 05:14
Last Modified:	31 May 2022 05:14
URI:	https://eprints.iisc.ac.in/id/eprint/72858