Sivakesavam, O and Prasad, YVRK (2022) Influence of homogenization on the processing map for hot working of as-cast Mg-2Zn-1Mn alloy. In: International Journal of Materials Research, 94 (11). pp. 1255-1259.
Full text not available from this repository.Abstract
Processing maps have been developed for hot deformation of Mg-2Zn- 1Mn alloy in as-cast condition and after homogenization with a view to evaluate the influence of homogenization. Hot compression data in the temperature range 300 - 500 °C and strain rate range 0.001 - 100 s- 1 were used for generating the processing map. In the map for the as-cast alloy the domain of dynamic recrystallization occurring at 450 °C and 0.1 s-1 has merged with another domain occurring at 500 °C and 0.001 s- 1 representing grain boundary cracking. The latter domain is eliminated by homogenization and the dynamic recrystallization domain expanded with a higher peak efficiency occurring at 500 °C and 0.05 s-1. The flow localization occurring at strain rates higher than 5 s-1 is unaffected by homogenization. © 2003 Carl Hanser Verlag, München.
Item Type: | Journal Article |
---|---|
Publication: | International Journal of Materials Research |
Publisher: | Walter de Gruyter GmbH |
Additional Information: | The copyright for this article belongs to Walter de Gruyter GmbH |
Keywords: | Cracks; Dynamic recrystallization; Grain boundaries; Hot working; Magnesium alloys; Manganese alloys; Strain rate; Ternary alloys, As cast alloy; As-cast; Compression data; Condition; Dynamic recrystallisation; Grain boundary cracking; Homogenization; Processing maps; Strain-rates; Temperature range, Zinc alloys |
Department/Centre: | Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy) |
Date Deposited: | 16 Mar 2022 06:04 |
Last Modified: | 16 Mar 2022 06:04 |
URI: | http://eprints.iisc.ac.in/id/eprint/71422 |
Actions (login required)
![]() |
View Item |