Suresh, M and Sharma, A and More, A M and Nayan, N and Suwas, S (2015) Effect of Scandium addition on evolution of microstructure, texture and mechanical properties of thermo-mechanically processed Al-Li alloy AA2195. In: JOURNAL OF ALLOYS AND COMPOUNDS, 740 . pp. 364-374.
PDF
Jou_All_COm_740_364_2018.pdf - Published Version Restricted to Registered users only Download (4MB) | Request a copy |
Abstract
In the present study, influence of Scandium (Sc) content (0.025 and 0.25 wt%) on microstructure, texture and mechanical properties of a thermo-mechanically processed AA2195 alloy has been investigated. Addition of Sc to AA2195 alloy results in grain refinement and enhanced precipitation kinetics. TEM analysis revealed the presence of Al-3(Sc,Zr) dispersoids in the Sc containing AA2195 alloys. Solution treatment and peak aging of the Sc containing alloys revealed partially recrystallized microstructure. Texture of Sc containing alloys displayed weaker Brass component compared to the Sc free material. A clear improvement in hardness and strength was observed which could be attributed to grain refinement as well as the presence of fine Al-3(Sc,Zr) dispersoids. Ductility decreased slightly on Sc addition and there was an associated change in fracture mode as a result of Sc addition. (C) 2017 Elsevier B.V. All rights reserved.
Item Type: | Journal Article |
---|---|
Publication: | JOURNAL OF ALLOYS AND COMPOUNDS |
Publisher: | ELSEVIER SCIENCE SA, PO BOX 564, 1001 LAUSANNE, SWITZERLAND |
Additional Information: | Copy right for the article belong to ELSEVIER SCIENCE SA, PO BOX 564, 1001 LAUSANNE, SWITZERLAND |
Department/Centre: | Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy) |
Date Deposited: | 14 Mar 2018 17:40 |
Last Modified: | 14 Mar 2018 17:40 |
URI: | http://eprints.iisc.ac.in/id/eprint/59153 |
Actions (login required)
View Item |