A Surlyn/magnesium oxide nanocomposite as an effective water vapor barrier for organic device encapsulation

Kopanati, Gayathri N and Seethamraju, Sindhu and Ramamurthy, Praveen C and Madras, Giridhar (2015) A Surlyn/magnesium oxide nanocomposite as an effective water vapor barrier for organic device encapsulation. In: RSC ADVANCES, 5 (41). pp. 32580-32587.

[img] PDF
rsc_adv-5_41_32580_2015.pdf - Published Version
Restricted to Registered users only

Download (984kB) | Request a copy
Official URL: http://dx.doi.org/10.1039/c5ra03356j

Abstract

A reactive polymer nanocomposite system was proposed as an effective water vapor barrier material for organic device encapsulation. Nanosized magnesium oxide (MgO) was synthesized by the solution combustion technique using two different fuels, lactose and alanine. The purity and crystallite size of MgO were determined from X-ray diffraction studies. The surface areas and porosity measurements were used to determine the water adsorption capacities of MgO. Nanocomposites with various concentrations (wt% = 0.25, 0.5, 1 and 2.5) of MgO were prepared using Surlyn as the base polymer. The permeation rate of moisture through the fabricated films was calculated using calcium degradation test and these rates were further used to calculate the diffusivities. Accelerated aging experiments were conducted to study the performance of organic photovoltaic devices encapsulated with synthesized films under accelerated weathering conditions. The performance of the barrier materials with synthesized MgO was also compared to that obtained with commercial MgO. The films containing MgO obtained from lactose exhibited better barrier properties compared to other films made with commercial MgO and MgO synthesized using alanine as well as other nanocomposites reported in the literature.

Item Type: Journal Article
Publication: RSC ADVANCES
Publisher: ROYAL SOC CHEMISTRY
Additional Information: Copy right for this article belongs to the ROYAL SOC CHEMISTRY, THOMAS GRAHAM HOUSE, SCIENCE PARK, MILTON RD, CAMBRIDGE CB4 0WF, CAMBS, ENGLAND
Keywords: SOLUTION COMBUSTION SYNTHESIS; LIGHT-EMITTING DEVICES; MOISTURE BARRIER; PHOTOCATALYTIC ACTIVITY; CLAY CONCENTRATION; GAS BARRIER; FILMS; DEGRADATION; BEHAVIOR; LAYERS
Department/Centre: Division of Mechanical Sciences > Chemical Engineering
Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Division of Interdisciplinary Sciences > Centre for Nano Science and Engineering
Date Deposited: 22 May 2015 09:25
Last Modified: 22 May 2015 09:25
URI: http://eprints.iisc.ac.in/id/eprint/51591

Actions (login required)

View Item View Item