Synthesis of Eu3+-activated BiOF and BiOBr phosphors: photoluminescence, Judd-Ofelt analysis and photocatalytic properties

Saraf, Rohit and Shivakumara, C and Behera, Sukanti and Dhananjaya, N and Nagabhushana, H (2015) Synthesis of Eu3+-activated BiOF and BiOBr phosphors: photoluminescence, Judd-Ofelt analysis and photocatalytic properties. In: RSC ADVANCES, 5 (12). pp. 9241-9254.

PDF rsc_adv_5-12_2015.pdf.pdf - Published Version Restricted to Registered users only Download (2MB) | Request a copy

Abstract

A series of Bi1-xEuxOX (X = F and Br; x = 0, 0.01, 0.03 and 0.05) phosphors were synthesized at relatively low temperature and short duration (500 degrees C, 1 h). Rietveld refinement results verified that all the compounds were crystallized in the tetragonal structure with space group P4/nmm (no. 129). Photoluminescence spectra exhibit characteristic luminescence D-5(0) -> F-7(J) (J = 0-4) intra-4f shell Eu3+ ion transitions. The magnetic dipole (D-5(0) -> F-7(1)) transition dominates the emission of BiOF:Eu3+, while the electric dipole (D-5(0) -> F-7(2)) peak was stronger in BiOBr:Eu3+ phosphors. The evaluated CIE color coordinates for Bi0.95Eu0.05OBr (0.632, 0.358) are close to the commercial Y2O3:Eu3+ (0.645, 0.347) and Y2O2S:Eu3+ (0.647, 0.343) red phosphors. Intensity parameters (Omega(2), Omega(4)) and various radiative properties such as transition rates (A), branching ratios (beta), stimulated emission cross-section (sigma(e)), gain bandwidth (sigma(e) x Delta lambda(eff)) and optical gain (sigma(e) x tau) were calculated using the Judd-Ofelt theory. It was observed that BiOBr:Eu3+ phosphors have a long lifetime (tau) and better optical gain (sigma(e) x tau) as compared to reported Eu3+ doped materials. Furthermore, these compounds exhibit excellent photocatalytic activity for the degradation of rhodamine B dye under visible light irradiation. The determined radiative properties and photocatalytic results revealed that BiOBr:Eu3+ phosphors have potential applications in energy and environmental remedies, such as to develop red phosphors for white light-emitting diodes, red lasers and to remove toxic organic industrial effluents.

Item Type:	Journal Article
Publication:	RSC ADVANCES
Publisher:	ROYAL SOC CHEMISTRY
Additional Information:	Copy right for this article belongs to the ROYAL SOC CHEMISTRY, THOMAS GRAHAM HOUSE, SCIENCE PARK, MILTON RD, CAMBRIDGE CB4 0WF, CAMBS, ENGLAND
Department/Centre:	Division of Chemical Sciences > Solid State & Structural Chemistry Unit
Date Deposited:	19 Mar 2015 12:10
Last Modified:	19 Mar 2015 12:10
URI:	http://eprints.iisc.ac.in/id/eprint/51060

Actions (login required)

View Item