Dielectric properties of (110) oriented PbZrO3 and La-modified PbZrO3 thin films grown by sol-gel process on Pt(111)/Ti/SiO2/Si substrate

Parui, Jayanta and Krupanidhi, SB (2006) Dielectric properties of (110) oriented PbZrO3 and La-modified PbZrO3 thin films grown by sol-gel process on Pt(111)/Ti/SiO2/Si substrate. In: Journal of Applied Physics , 100 (4). 044102-044102.

PDF Dielectric_properties.pdf - Published Version Restricted to Registered users only Download (879kB) | Request a copy

Abstract

Highly (110) preferred orientated antiferroelectric PbZrO3 (PZ) and La-modified PZ thin films have been fabricated on Pt/Ti/SiO2/Si substrates using sol-gel process. Dielectric properties, electric field induced ferroelectric polarization, and the temperature dependence of the dielectric response have been explored as a function of composition. The Tc has been observed to decrease by ∼ 17 °C per 1 mol % of La doping. Double hysteresis loops were seen with zero remnant polarization and with coercive fields in between 176 and 193 kV/cm at 80 °C for antiferroelectric to ferroelectric phase transformation. These slim loops have been explained by the high orientation of the films along the polar direction of the antiparallel dipoles of a tetragonal primitive cell and by the strong electrostatic interaction between La ions and oxygen ions in an ABO3 perovskite unit cell. High quality films exhibited very low loss factor less than 0.015 at room temperature and pure PZ; 1 and 2 mol % La doped PZs have shown the room temperature dielectric constant of 135, 219, and 142 at the frequency of 10 kHz. The passive layer effects in these films have been explained by Curie constants and Curie temperatures. The ac conductivity and the corresponding Arrhenius plots have been shown and explained in terms of doping effect and electrode resistance.

Item Type:	Journal Article
Publication:	Journal of Applied Physics
Publisher:	American Institute of Physics
Additional Information:	Copyright of this article belongs to American Institute of Physics.
Department/Centre:	Division of Chemical Sciences > Materials Research Centre
Date Deposited:	27 Feb 2012 11:08
Last Modified:	27 Feb 2012 11:08
URI:	http://eprints.iisc.ac.in/id/eprint/43022

Actions (login required)

View Item