Growth of nanowires of beta-NaxV2O5 by metalorganic chemical vapor deposition

Sahana, MB and Shivashankar, SA (2003) Growth of nanowires of beta-NaxV2O5 by metalorganic chemical vapor deposition. In: Journal of Materials Chemistry, 13 (9). pp. 2254-2260.

[img] PDF
Growth_of_nanowires.pdf - Published Version
Restricted to Registered users only

Download (596kB) | Request a copy
Official URL: http://pubs.rsc.org/en/Content/ArticleLanding/2003...


Films comprised of nanowires of beta-NaxV2O5 measuring 20-200 nm in diameter and 10-30 mum in length have been prepared on glass substrates by metalorganic chemical vapor deposition using the beta-diketonate complex, vanadyl acetyl acetonate, as precursor, but without the use of either templates or catalysts. Films consisting of nanowires of monophasic beta-NaxV2O5 with a preferred orientation along (h0l) are formed only at 550 degreesC, whereas those deposited at 540 degreesC comprise a mixture of nanowires (beta-NaxV2O5) and platelets (V2O5). The films deposited at lower temperatures are less crystalline and comprise a mixture of vanadium oxide phases. From the observations that nanowires are formed only in the narrow temperature range of 540-550 degreesC, and from the critical dependence of the formation of nanowires on the balance between the CVD growth rate and the evaporation rate of the film, it is inferred that the formation of nanowires of beta-NaxV2O5 is due to chemical vapor transport.

Item Type: Journal Article
Publication: Journal of Materials Chemistry
Publisher: Royal Society of Chemistry
Additional Information: Copyright of this article belongs to Royal Society of Chemistry.
Department/Centre: Division of Chemical Sciences > Materials Research Centre
Date Deposited: 29 Aug 2011 07:14
Last Modified: 29 Aug 2011 07:14
URI: http://eprints.iisc.ac.in/id/eprint/40105

Actions (login required)

View Item View Item