Alam, Zafir Md and Chatterjee, Debarati and Muraleedharan, K and Nandy, TK and Kamat, SV and Jayaram, V and Das, DK (2011) Effect of Strain Rate on Ductile-to-Brittle Transition Temperature of a Free-Standing Pt-Aluminide Bond Coat. In: Metallurgical and Materials Transactions A, 42 (6). pp. 1431-1434.
![]() |
PDF
Effect.pdf - Published Version Restricted to Registered users only Download (432kB) | Request a copy |
Abstract
The ductile-to-brittle transition temperature (DBTT) of a free-standing Pt-aluminide (PtAl) bondcoat was determined using the microtensile testing method and the effect of strain rate variation, in the range 10(-5) to 10(-1) s(-1), on the DBTT studied. The DBTT increased appreciably with the increase in strain rate. The activation energy determined for brittle-to-ductile transition, suggested that such transition is most likely associated with vacancy diffusion. Climb of aOE (c) 100 > dislocations observed in analysis of dislocation structure using a transmission electron microscope (TEM) supported the preceding mechanism.
Item Type: | Journal Article |
---|---|
Publication: | Metallurgical and Materials Transactions A |
Publisher: | Springer |
Additional Information: | Copyright of this article belongs to Springer. |
Department/Centre: | Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy) |
Date Deposited: | 01 Jun 2011 11:40 |
Last Modified: | 19 Jul 2011 12:08 |
URI: | http://eprints.iisc.ac.in/id/eprint/37801 |
Actions (login required)
![]() |
View Item |