Flow Instabilities and fracture in Ti-6Al-4V deformed in compression at 298 K to 673 K

Kailas, SV and Prasad, YVRK and Biswas, SK (1994) Flow Instabilities and fracture in Ti-6Al-4V deformed in compression at 298 K to 673 K. In: Metallurgical and materials transactions a, 25 (10). 2173-2179 .

[img] PDF
flat_instbilities.pdf - Published Version
Restricted to Registered users only

Download (2MB) | Request a copy
Official URL: http://www.springerlink.com/content/y17582u3860127...


Uniaxial compression tests were conducted on Ti-6Al-4V specimens in the strain-rate range df 0.001 to 1 s(-1) and temperature range of 298 to 673 K. The stress-strain curves exhibited a peak flow stress followed by flow softening. Up to 523 K, the specimens cracked catastrophically after the flow softening started. Adiabatic shear banding was observed in this regime. The fracture surface exhibited both mode I and II fracture features. The state of stress existing in a compression test specimen when bulging occurs is responsible for this fracture. The instabilities observed in the present tests are classified as ''geometric'' in nature and are state-of-stress dependant, unlike the ''intrinsic'' instabilities, which are dependant on the dynamic constitutive behavior of the material.

Item Type: Journal Article
Publication: Metallurgical and materials transactions a
Publisher: The minerals,metals & materials society
Additional Information: Copyright of this article belongs to The minerals,metals & materials society.
Department/Centre: Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited: 13 Apr 2011 05:25
Last Modified: 13 Apr 2011 05:25
URI: http://eprints.iisc.ac.in/id/eprint/36480

Actions (login required)

View Item View Item