Large negative magnetoresistance and metal-insulator transition observed in MnO/C composite coatings grown on ceramic alumina by metalorganic chemical vapor deposition

Varade, Ashish and Shivashankar, SA (2011) Large negative magnetoresistance and metal-insulator transition observed in MnO/C composite coatings grown on ceramic alumina by metalorganic chemical vapor deposition. In: Carbon, 49 (4). pp. 1401-1407.

PDF Large.pdf - Published Version Restricted to Registered users only Download (798kB) | Request a copy

Abstract

MnO/C composite coatings were grown by the metalorganic chemical vapor deposition process on ceramic alumina in argon ambient. Characterization by various techniques confirms that these coatings are homogeneous composites comprising nanometer-sized MnO particles embedded in a matrix of nanometer-sized graphite. Components of the MnO/C composite coating crystalline disordered, but are electrically quite conductive. Resistance vs. temperature measurements show that coating resistance increases exponentially from a few hundred ohms at room temperature to a few megaohms at 30 K. Logarithmic plots of reduced activation energy vs. temperature show that the coating material undergoes a metal-insulator transition. The reduced activation energy exponent for the film under zero magnetic field was 2.1, which is unusually high, implying that conduction is suppressed at much faster rate than the Mott or the Efros-Shklovskii hopping mechanism. Magnetoconductance us. magnetic field plots obtained at various temperatures show a high magnetoconductance (similar to 28.8%) at 100 K, which is unusually large for a disordered system, wherein magnetoresistance is attributed typically to weak localization. A plausible explanation for the unusual behavior observed in the carbonaceous disordered composite material is proposed. (C) 2010 Elsevier Ltd. All rights reserved.

Item Type:	Journal Article
Publication:	Carbon
Publisher:	Elsevier Science
Additional Information:	Copyright of this article belongs to Elsevier Science.
Department/Centre:	Division of Chemical Sciences > Materials Research Centre
Date Deposited:	14 Mar 2011 06:19
Last Modified:	14 Mar 2011 06:19
URI:	http://eprints.iisc.ac.in/id/eprint/36048

Actions (login required)

View Item