Phase relations and thermodynamic properties of condensed phases in the system calcium-copper-oxygen

Mathews, Tom and Hajra, JP and Jacob, KT (1993) Phase relations and thermodynamic properties of condensed phases in the system calcium-copper-oxygen. In: Chemistry of Materials, 5 (11). 1669-1675 .

[img] PDF
Thermo.pdf - Published Version
Restricted to Registered users only

Download (760kB) | Request a copy
Official URL: http://pubs.acs.org/doi/abs/10.1021/cm00035a014

Abstract

The isothermal sections of the phase diagram for the system Ca-Cu-0 at 1073 and 1223 K have been determined. Several compositions in the ternary system were quenched after equilibration, and the phases present were identified by optical microscopy, X-ray diffraction, and electron probe microanalysis. Two ternary compounds Ca2CuO3 and Cao.8&uO1.9s were identified at 1073 K. However, only Ca2CuO3 was found to be stable at 1223 K. The thermodynamic properties of the two ternary compounds were determined using solid-state cells incorporating either an oxide or a fluoride solid electrolyte. The results for both types of cells were internally consistent. The compound C ~ O . ~ & U Ow~h.i~ch~ c, a n also be represented as Ca15Cu18035h, as been identified in an earlier investigation as Cao.828CuOz. Using a novel variation of the galvanic cell technique, in which the emf of a cell incorporating a fluoride electrolyte is measured as a function of the oxygen potential of the gas phase in equilibrium with the condensed phase electrodes, it has been confirmed that the compound Cao.828CuO1.93 (Ca15Cu18035d) oes not have significant oxygen nonstoichiometry. Phase relations have been deduced from the thermodynamic data as a function of the partial pressure of oxygen for the system Ca-Cu-0 at 873, 1073, and 1223 K.

Item Type: Journal Article
Publication: Chemistry of Materials
Publisher: American Chemical Society
Additional Information: Copyright of this article belongs to American Chemical Society.
Department/Centre: Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited: 18 Feb 2011 07:31
Last Modified: 18 Feb 2011 07:31
URI: http://eprints.iisc.ac.in/id/eprint/35669

Actions (login required)

View Item View Item