Jayanthi, S and Kutty, TRN (2006) Dielectric properties of barium magnesiotitanate ceramics, BaMg6Ti6O19. In: Materials Letters, 60 (6). pp. 796-800.
PDF
sdarticle.pdf - Published Version Restricted to Registered users only Download (321kB) | Request a copy |
Abstract
Phase-pure samples of barium magnesiotitanate, BaMg6Ti6O19 (BMT) are prepared by the wet chemical `gel-carbonate' method wherein the formation of BMT is complete below 950 degrees C as a result of the reaction between nanoparticles of BaCO3, MgO and TiO2. BMT powders are sintered at 1350-1450 C to dense ceramics. Extensive melting is noticed when the bulk composition falls between 0.4MgTiO(3)+0.6BaTiO(3)) and (0.6MgTiO(3)+0.4BaTiO(3)) along the MgTiO3-BaTiO3 tie-line in BaO-MgO-TiO2, phase diagram. Dielectric properties of sintered (BMT) ceramics have been investigated which showed epsilon similar or equal to 39 at 2 GHz, quality factor Q >= 10,000 and positive temperature coefficient of dielectric constant around 370 ppm degrees C-1.
Item Type: | Journal Article |
---|---|
Publication: | Materials Letters |
Publisher: | Elsevier Science |
Additional Information: | Copyright of this article belongs to Elsevier Science. |
Keywords: | Ceramics;Processing;Sintering;Microstructure;Dielectrics. |
Department/Centre: | Division of Chemical Sciences > Materials Research Centre |
Date Deposited: | 02 Sep 2010 09:01 |
Last Modified: | 19 Sep 2010 06:15 |
URI: | http://eprints.iisc.ac.in/id/eprint/31923 |
Actions (login required)
View Item |