Interfacial coupling and its size dependence in PbTiO3 and PbMg1/3Nb2/3O3 multilayers

Ranjith, R and Nikhil, R and Krupanidhi, SB (2006) Interfacial coupling and its size dependence in PbTiO3 and PbMg1/3Nb2/3O3 multilayers. In: Physical Review B, 74 (18).

[img] PDF
e184104.pdf - Published Version
Restricted to Registered users only

Download (297kB) | Request a copy
Official URL: http://prb.aps.org/abstract/PRB/v74/i18/e184104


Multilayers of Pb(Mg1/3Nb2/3)O-3 (PMN)-PbTiO3 (PT) were deposited through pulsed laser ablation deposition with different periodicities (d=10, 20, 30, 40, 50, 60, and 70 nm) for a constant total thickness of the film. The presence of superlattice reflections in the x-ray diffraction pattern clearly showed the superlattice behavior of the fabricated structures over a periodicity range of 20-50 nm. Polarization hysteresis and the capacitance-voltage characteristics of these films show clear size dependent ferroelectric and antiferroelectric (AFE) characteristics. Presence of long-range coupling and strain in multilayers with lower periodicity (similar to 10 nm) exhibited a clear ferroelectric behavior similar to a solid solution of PMN and PT. Multilayers with higher periodicities (20-50 nm) exhibited antiferroelectric behavior, which could be understood from the energy arguments. On further increase of periodicity, they again exhibit ferroelectric behavior. The polarization studies were carried out beyond the Curie temperature T-c of PMN to understand the interlayer interaction. The interaction is changed to a ferroelectric-paraelectric interlayer and tends to lose its antiferroelectric behavior. The behavior of remnant polarization P-r and dP(r)/dT with temperature clearly proves that the AFE coupling of these superlattices is due to the extrinsic interfacial coupling and not an intrinsic interaction as in a homogeneous conventional AFE material. The evidence of an averaged behavior at a periodicity of similar to 10 nm, and the behavior of individual materials at larger periodicities were further confirmed through dielectric phase transition studies. The presence of AFE interfacial coupling was insignificant over the dielectric phase transition of the multilayers.

Item Type: Journal Article
Publication: Physical Review B
Publisher: American Physical Society
Additional Information: Copyright of this article belongs to American Physical Society.
Department/Centre: Division of Chemical Sciences > Materials Research Centre
Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited: 03 Aug 2010 06:10
Last Modified: 19 Sep 2010 06:12
URI: http://eprints.iisc.ac.in/id/eprint/30729

Actions (login required)

View Item View Item