High Rate Capability of Porous LiNi1/3Co1/3Mn1/3O2 Synthesized by Polymer Template Route

Sinha, NN and Munichandraiah, N (2010) High Rate Capability of Porous LiNi1/3Co1/3Mn1/3O2 Synthesized by Polymer Template Route. In: Journal of the Electrochemical Society, 157 (6). A647-A653.

[img] PDF
Poly.pdf - Published Version
Restricted to Registered users only

Download (985kB) | Request a copy
Official URL: http://scitation.aip.org/getabs/servlet/GetabsServ...

Abstract

Layered LiNi1/3Co1/3Mn1/3O2, which is isostructural with LiCoO2, is considered as a potential cathode material for Li-ion batteries. Submicrometer sized porous particles are useful for high discharge rates. The present work involves a synthesis of submicrometer sized porous particles of LiNi1/3Co1/3Mn1/3O2 using a triblock copolymer as a soft template. The precursor obtained from the reaction is heated at different temperatures between 600 and 900 degrees C for 6 h to get the final product samples. The compound attains increased crystallinity with an increase in the temperature of preparation. However, there is a decrease in the surface area and also in the porosity of the sample. Nevertheless, the LiNi1/3Co1/3Mn1/3O2 sample prepared at 900 degrees C exhibits a high rate capability and stable capacity retention on cycling. The electrochemical performance of LiNi1/3Co1/3Mn1/3O2 prepared in the absence of the polymer template is inferior to that of the sample prepared in the presence of the polymer template. (C) 2010 The Electrochemical Society. [DOI: 10.1149/1.3364944] All rights reserved.

Item Type: Journal Article
Publication: Journal of the Electrochemical Society
Publisher: The Electrochemical Society
Additional Information: Copyright of this article belongs to The Electrochemical Society.
Department/Centre: Division of Chemical Sciences > Inorganic & Physical Chemistry
Date Deposited: 15 Jul 2010 09:45
Last Modified: 19 Sep 2010 06:10
URI: http://eprints.iisc.ac.in/id/eprint/28936

Actions (login required)

View Item View Item