Dielectric relaxation and electrical conductivity in Bi5NbO10 oxygen ion conductors prepared by a modified sol–gel process

Hou, Jungang and Vaish, Rahul and Qu, Yuanfang and Krsmanovic, Dalibor and Varma, KBR and Kumar, RV (2010) Dielectric relaxation and electrical conductivity in Bi5NbO10 oxygen ion conductors prepared by a modified sol–gel process. In: Journal of Power Sources, 195 (9). pp. 2613-2618.

[img] PDF
Relax.pdf - Published Version
Restricted to Registered users only

Download (1MB) | Request a copy
Official URL: http://dx.doi.org/10.1016/j.jpowsour.2009.11.081


Crystalline Bi5NbO10 nanoparticles have been achieved through a modified sol–gel process using a mixture of ethylenediamine and ethanolamine as a solvent. The Bi5NbO10 nanoparticles were characterized by X-ray diffraction (XRD), differential scanning calorimetry/thermogravimetry (DSC/TG), Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM) and Raman spectroscopy. The results showed that well-dispersed 5–60 nm Bi5NbO10 nanoparticles were prepared through heat-treating the precursor at 650 °C and the high density pellets were obtained at temperatures lower than those commonly employed. The frequency and temperature dependence of the dielectric constant and the electrical conductivity of the Bi5NbO10 solid solutions were investigated in the 0.1 Hz to 1 MHz frequency range. Two distinct relaxation mechanisms were observed in the plots of dielectric loss and the imaginary part of impedance (Z″) versus frequency in the temperature range of 200–350 °C. The dielectric constant and the loss in the low frequency regime were electrode dependent. The ionic conductivity of Bi5NbO10 solid solutions at 700 °C is 2.86 Ω−1 m−1 which is in same order of magnitude for Y2O3-stabilized ZrO2 ceramics at same temperature. These results suggest that Bi5NbO10 is a promising material for an oxygen ion conductor.

Item Type: Journal Article
Publication: Journal of Power Sources
Publisher: Elsevier Science
Additional Information: Copyright of this article belongs to Elsevier Science.
Department/Centre: Division of Chemical Sciences > Materials Research Centre
Date Deposited: 14 Jul 2010 05:16
Last Modified: 19 Sep 2010 06:10
URI: http://eprints.iisc.ac.in/id/eprint/28920

Actions (login required)

View Item View Item