Texture dependent stress corrosion failure of commercial titanium sheets in bromine-methanol solution

Nayak, HV Sudhaker and Vasu, KI and Prasad, YVRK (1980) Texture dependent stress corrosion failure of commercial titanium sheets in bromine-methanol solution. In: Journal of Materials Science, 15 (5). pp. 1265-1275.

[img] PDF
fulltext.pdf - Published Version
Restricted to Registered users only

Download (1MB) | Request a copy
Official URL: http://www.springerlink.com/content/r20427g6371110...


The stress corrosion cracking (SCC) characteristics of agr-titanium sheets in a bromine-methanol solution have been studied in the annealed and cold-rolled conditions using longitudinal and transverse specimens. The times to failure for annealed longitudinal specimens were longer than those for similarly tested transverse specimens. The cold-rolled specimens developed resistance to SCC, but failed by cleavage when notched, unlike the intergranular separation in annealed titanium. The apparent activation energy was found to be texture dependent and was in the range 30 to 51 kJ mol–1 for annealed titanium, and 15kJ mol–1 for cold-rolled titanium. The dependence of SCC behaviour on the texture is related to the changes in the crack initiation times. These are caused by changes in the passivation and repassivation characteristics of the particular thickness plane. The thickness planes are identified with the help of X-ray pole figures obtained on annealed and cold-rolled material. On the basis of the activation energy and the electrochemical measurements, the mechanism of SCC in annealed titanium is identified to be the one involving stress-aided anodic dissolution. On the other hand, the results on the cold-rolled titanium are in support of the hydrogen embrittlement mechanism consisting of hydride precipitation. The cleavage planes identified from the texture data match with the reported habit planes for hydride formation.

Item Type: Journal Article
Publication: Journal of Materials Science
Publisher: Springer
Additional Information: Copyright of this article belongs to Springer.
Department/Centre: Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited: 05 Feb 2010 06:28
Last Modified: 19 Sep 2010 05:42
URI: http://eprints.iisc.ac.in/id/eprint/22476

Actions (login required)

View Item View Item