Subba Reddy, B (2019) Failure analysis of BMC insulators used for third rail traction system. In: Engineering Failure Analysis, 101 . pp. 1-8.
![]() |
PDF
Eng_Fai_Ana_101_1-8_2019.pdf - Published Version Restricted to Registered users only Download (2MB) | Request a copy |
Abstract
Bulk molding compound (BMC) or Glass Reinforced plastic (GRP) composite insulators are extensively used for the third rail electric traction system. The performance of these insulators primarily depends on the local environmental conditions that cause degradation over a period of time. Degradation leads to partial arcing which grow more severe and can generate combustion that ignites flammable debris, smoke including fires resulting in service interruptions and safety risks of the third rail traction system. In the present investigations, exhaustive analysis is conducted to understand the root cause of degradation and arcing on the field aged insulators rated for 750Vdc. Leakage current and surface resistance measurements are conducted under dry, wet and contaminated conditions. Further to better interpret Physico-chemical analysis are conducted using Scanning Electron Microscopy (SEM), Energy Dispersive X-Ray (EDAX) and Fourier Transform Infra-Red (FTIR) spectroscopy to investigate surface morphology and chemical changes in the samples, also Thermo-Gravimetric Analysis (TGA) is performed to find the thermal characteristics of the insulator. Interesting results obtained from the investigations clearly present evidence to loss of epoxy material from the bulk eventually leading to the exposure of glass fibers causing degradation, arcing and failure of the insulators. The study further highlights the essential procedures to be edopted to locate, isolate, and better anticipate failures of BMC insulators used in third rail traction system. © 2019 Elsevier Ltd
Item Type: | Journal Article |
---|---|
Publication: | Engineering Failure Analysis |
Publisher: | Elsevier Ltd |
Additional Information: | Copyright belongs to Elsevier Ltd |
Keywords: | Degradation; Energy dispersive spectroscopy; Failure (mechanical); Fourier transform infrared spectroscopy; Glass fibers; Gravimetric analysis; Leakage currents; Pultrusion; Reinforced plastics; Scanning electron microscopy; Smoke; Thermogravimetric analysis, Electric traction system; Environmental conditions; Fourier transform infra red (FTIR) spectroscopy; FTIR; Glass reinforced plastics; Physico-chemical analysis; Rail traction; Surface resistance measurements, Electric current collection |
Department/Centre: | Division of Electrical Sciences > Electrical Engineering |
Date Deposited: | 16 Apr 2019 06:49 |
Last Modified: | 16 Apr 2019 06:49 |
URI: | http://eprints.iisc.ac.in/id/eprint/62135 |
Actions (login required)
![]() |
View Item |