Processing and nanoclay induced piezoelectricity in poly(vinylidene fluoride-co-hexafluoro propylene) nanohybrid for device application

Gaur, Anupama and Shukla, Rahul and Brajesh, Kumar and Pal, Arkadeb and Chatterji, Sandeep and Ranjan, Rajeev and Maiti, Pralay (2016) Processing and nanoclay induced piezoelectricity in poly(vinylidene fluoride-co-hexafluoro propylene) nanohybrid for device application. In: POLYMER, 97 . pp. 362-369.

PDF Pol_97_362_2016.pdf - Published Version Restricted to Registered users only Download (1MB) | Request a copy

Abstract

Process and nanoparticle induced piezoelectric super toughened poly(vinylidene fluoride-co-hexafluoro propylene) (HFP) nanohybrids have been developed for device application. The nanohybrids have been prepared by incorporating organically modified nanoclay through solution route. The nanohybrids show improvement in toughness and modulus along with piezoelectric phases compared to pure HFP. Piezoelectric phase has further enhanced to 75% in nanohybrid after uniaxial stretching of the thin film at moderately high temperature as compared to meager 18% beta-phase before stretching. The structural changes including quantitative measurements have been confirmed through X-ray diffraction, spectro-scopic and thermal studies. The structural and morphological origins of super toughening phenomena have been worked out. The piezoelectric and pyroelectric coefficients (d33 and p) exhibit significant increase after stretching at high temperature and the relative improvements are more in nanohybrid than that of pure HFP, arising from the presence of greater amount of b-phase in nanohybrid. The effect of structure on ferroelectricity has been studied through polarization-electric field hysteresis loop confirming greater maximum polarization, remnant polarization and coercive field for nanohybrid against pure HFP. Finally, fabrication of the unimorph has been performed using the high piezoelectric coefficient materials. The greater voltage generation under impulse load is demonstrated for nanohybrid along with longer time response vis-a-vis pure HFP clearly indicating the superior piezoelectric device made using nanohybrid where the extent of piezoelectric phase is considerably higher. (C) 2016 Elsevier Ltd. All rights reserved.

Item Type:	Journal Article
Publication:	POLYMER
Publisher:	ELSEVIER SCI LTD
Additional Information:	Copy right for this article belongs to the ELSEVIER SCI LTD, THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, OXON, ENGLAND
Keywords:	Fluoropolymer; Nanohybrid; Structure; Piezo- and pyroelectricity; Device
Department/Centre:	Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited:	19 Aug 2016 05:38
Last Modified:	19 Aug 2016 05:38
URI:	http://eprints.iisc.ac.in/id/eprint/54389

Actions (login required)

View Item