Spark plasma sintering of novel ZrB2-SiC-TiSi2 composites with better mechanical properties

Gupta, Neha and Mukhopadhyay, Amartya and Pavani, K and Basu, Bikramjit (2012) Spark plasma sintering of novel ZrB2-SiC-TiSi2 composites with better mechanical properties. In: Materials Science and Engineering: A, 534 . pp. 111-118.

PDF mat_sci_engA_534_111-118_2012.pdf - Published Version Restricted to Registered users only Download (2MB) | Request a copy

Abstract

We report here the development of ultrafine grained ZrB2-SiC composites using TiSi2 as the sintering aid and spark plasma sintering (SPS) as the processing technique. It was observed that the presence of TiSi2 improved the sinterability of the composites, such that near theoretical densification (99.9%) could be achieved for ZrB2-18 wt.% SiC-5 wt.% TiSi2 composites after SPS at 1600 degrees C for 10 min at 50 MPa. Use of innovative multi stage sintering (MSS) route, which involved holding the samples at lower (intermediate) temperatures for some time before holding at the final temperature, while keeping the net holding time to 10 min, allowed attainment of full densification of ZrB2-18 wt.% SiC-2.5 wt.% TiSi2 at a still lower final temperature of 1500 degrees C at 30 MPa. TEM observations, which revealed the presence of anisotropic ZrB2 grains with faceted grain boundaries and TiSi2 at the intergranular regions, suggested the occurrence of liquid phase sintering in the presence of TiSi2. No additional phase was detected in XRD as well as TEM, which confirmed the absence of any sintering reaction. The as developed composites possessed an excellent combination of Vickers hardness and indentation toughness, both of which increased with increase in TiSi2 content, such that the ZrBi2-18 wt.% SiC-5 wt.% TiSi2 (SPS processed at 1600 degrees C) possessed hardness of similar to 20 GPa and indentation toughness of similar to 5 MPa m(1/2). The use of MSS SPS at 1500 degrees C for ZrBi2-18 wt.% SiC-2.5 wt.% TiSi2 composite resulted in improvement in hardness of up to similar to 27 GPa and attainment of high flexural strength of similar to 455 MPa. (C) 2011 Elsevier B.V. All rights reserved.

Item Type:	Journal Article
Publication:	Materials Science and Engineering: A
Publisher:	Elsevier Science
Additional Information:	Copyright of this article belongs to Elsevier Science.
Keywords:	Spark plasma sintering; ZrB2; Microstructure; Mechanical properties
Department/Centre:	Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited:	18 May 2012 07:56
Last Modified:	18 May 2012 07:58
URI:	http://eprints.iisc.ac.in/id/eprint/44408

Actions (login required)

View Item