Vaish, Rahul and Varma, KBR (2009) Low loss and frequency (1 kHz-1 MHz) independent dielectric characteristics of 3BaO-3TiO(2)-B2O3 glasses. In: Journal of applied physics, 106 (11).
PDF
4.pdf - Published Version Restricted to Registered users only Download (503kB) | Request a copy |
Abstract
X-ray powder diffraction along with differential thermal analysis carried out on the as-quenched samples in the 3BaO-3TiO(2)-B2O3 system confirmed their amorphous and glassy nature, respectively. The dielectric constants in the 1 kHz-1 MHz frequency range were measured as a function of temperature (323-748 K). The dielectric constant and loss were found to be frequency independent in the 323-473 K temperature range. The temperature coefficient of dielectric constant was estimated using Havinga's formula and found to be 16 ppm K-1. The electrical relaxation was rationalized using the electric modulus formalism. The dielectric constant and loss were 17 +/- 0.5 and 0.005 +/- 0.001, respectively at 323 K in the 1 kHz-1 MHz frequency range which may be of considerable interest to capacitor industry.
Item Type: | Journal Article |
---|---|
Publication: | Journal of applied physics |
Publisher: | American Institute of Physics |
Additional Information: | Copyright for this article belongs to American Institute of Physics. |
Keywords: | amorphous state; barium compounds; boron compounds; dielectric losses; dielectric relaxation; differential thermal analysis; glass; permittivity; titanium compounds; vitreous state; X-ray diffraction |
Department/Centre: | Division of Chemical Sciences > Materials Research Centre |
Date Deposited: | 12 Jan 2010 09:20 |
Last Modified: | 19 Sep 2010 05:54 |
URI: | http://eprints.iisc.ac.in/id/eprint/25374 |
Actions (login required)
View Item |