Backward switching phenomenon from field forced ferroelectric to antiferroelectric phases in antiferroelectric PbZrO3 thin films

Bharadwaja, SSN and Krupanidhi, SB (2001) Backward switching phenomenon from field forced ferroelectric to antiferroelectric phases in antiferroelectric PbZrO3 thin films. In: Journal of Applied Physics, 89 (8). pp. 4541-4547.

PDF Backward_switching.pdf - Published Version Restricted to Registered users only Download (729kB) | Request a copy

Abstract

Antiferroelectric materials (example: lead zirconate and modified lead zirconate stannate), in which a field-induced ferroelectric phase transition is feasible due to a small free energy difference between the ferroelectric and the antiferroelectric phases, are proven to be very good candidates for applications involving actuation and high charge storage devices. The property of reverse switching from the field-induced ferroelectric to antiferroelectric phases is studied as a function of temperature, applied electric field, and sample thickness in antiferroelectric lead zirconate thin films deposited by pulsed excimer laser ablation. The maximum released charge density was 22 μC/cm2 from a stored charge density of 36 μC/cm2 in a 0.55 μ thick lead zirconate thin film. This indicated that more than 60% of the stored charge could be released in less than 7 ns at room temperature for a field of 200 kV/cm. The content of net released charge was found to increase with increasing field strength, whereas with increasing temperature the released charge was found to decrease. Thickness-dependent studies on lead zirconate thin films showed that size effects relating to extrinsic and intrinsic pinning mechanisms controlled the released and induced charges through the intrinsic switching time. These results proved that antiferroelectric PZ thin films could be utilized in high-speed charge decoupling capacitors in microelectronics applications.

Item Type:	Journal Article
Publication:	Journal of Applied Physics
Publisher:	American Institute of Physics
Additional Information:	Copyright of this article belongs to American Institute of Physics.
Department/Centre:	Division of Chemical Sciences > Materials Research Centre
Date Deposited:	23 Dec 2011 05:47
Last Modified:	23 Dec 2011 05:47
URI:	http://eprints.iisc.ac.in/id/eprint/42868

Actions (login required)

View Item