Tie lines and activities in the system NiO-MgO-SiO2 at 1373 K

Mukhopadhyay, S and Jacob, KT (1995) Tie lines and activities in the system NiO-MgO-SiO2 at 1373 K. In: Journal of Phase Equilibria, 16 (3). 243-253 .

[img] PDF
Tie_Lines_and.pdf - Published Version
Restricted to Registered users only

Download (992kB) | Request a copy
Official URL: http://www.springerlink.com/content/7h646040410677...


The isothermal section of the phase diagram for the system NiO-MgO-SiO2 at 1373 K is established, The tie lines between (NiXMg1-X)O solid solution with rock salt structure and orthosilicate solid solution (NiYMg1-Y)Si0.5O2 and between orthosilicate and metasilicate (NiZMg1-Z)SiO3 crystalline solutions are determined using electron probe microanalysis (EPMA) and lattice parameter measurement on equilibrated samples, Although the monoxides and orthosilicates of Ni and Mg form a continuous range of solid solutions, the metasilicate phase exists only for 0 < Z < 0.096, The activity of NiO in the rock salt solid solution is determined as a function of composition and temperature in the range of 1023 to 1377 K using a solid state galvanic cell, The Gibbs energy of mixing of the monoxide solid solution can be expressed by a pseudo-subregular solution model: Delta G(ex) = X(1 - X)[(-2430 + 0.925T)X + (-5390 + 1.758T)(1 - X)] J/mol, The thermodynamic data for the rock salt phase are combined with information on interphase partitioning of Ni and Mg to generate the mixing properties for the orthosilicate and the metasilicate solid solutions, The regular solution model describes the orthosilicate and the metasilicate solid solutions at 1373 K within experimental uncertainties, The regular solution parameter Delta G(ex)/Y(1 - Y) is -820 (+/-70) J/mol for the orthosilicate solid solution, The corresponding value for the metasilicate solid solution is -220 (+/-150) J/mol, The derived activities for the orthosilicate solid solution are discussed in relation to the intracrystalline ion exchange equilibrium between M1 and M2 sites. The tie line information, in conjunction with the activity data for orthosilicate and metasilicate solid solutions, is used to calculate the Gibbs energy changes for the intercrystalline ion exchange reactions, Combining this with the known data for NiSi0.5O2, Gibbs energies of formation of MgSi0.5O2, MgSiO3, and metastable NiSiO3 are calculated, The Gibbs energy of formation of NiSiO3, from its component oxides, is equal to 7.67 (+/-0.6) kJ/mol at 1373 K.

Item Type: Journal Article
Additional Information: Copyright of this article belongs to ASM International.
Department/Centre: Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Depositing User: Ms V Mangala
Date Deposited: 27 May 2011 06:25
Last Modified: 27 May 2011 06:25
URI: http://eprints.iisc.ac.in/id/eprint/37980

Actions (login required)

View Item View Item