Photoconductivity in β-AgI

Govindacharyulu, PA and Bose, DN (1979) Photoconductivity in β-AgI. In: Physical Review B: Condensed Matter, 19 (12). 6532-6541 .

[img] PDF
Photo.pdf - Published Version
Restricted to Registered users only

Download (1MB) | Request a copy
Official URL: http://prb.aps.org/abstract/PRB/v19/i12/p6532_1

Abstract

Excitation spectra and transient and steady-state photoconductivity have been studied in undoped and 0.8-mole% Cu-doped single-crystal β-AgI between 150 and 260°K. A single peak in the spectral response was found to occur in each case, at 2.88 eV for undoped and at 2.81 eV for copper-doped specimens at 260 K, the difference being due to a decrease in band gap. The anisotropy due to polarization of incident radiation parallel or perpendicular to the c direction, which is a measure of the energy difference between the Γ9 and Γ7 levels in the valence band, was found to be 0.010 eV. Transient-photoconductivity experiments showed that the hole lifetime was 6 μ sec at 300°K, an order of magnitude larger than the electron lifetime. The hole drift mobility was found to be 12±2 cm2/ V sec at 300°K and limited by traps at a depth of 0.51±0.01 eV with concentration (3-5)×109/cm3 and capture cross section 10-11 cm2. The study of photoconductivity decay versus temperature revealed the presence of shallow hole traps at 0.14±0.02 eV with concentration greater than 1016/cm3 and capture cross section 10-19 cm2. The steady-state photoconductivity was determined by the deep hole traps at 0.51 eV, and showed the presence of shallow electron traps at a depth of 0.28 eV. The trap distribution was found to be substantially the same in pure and copper-doped specimens, indicating the monovalent substitutional role of copper. The effects of iodine annealing, cadmium doping, and heating above the transition temperature were also studied. The possible nature of the traps is discussed.

Item Type: Journal Article
Publication: Physical Review B: Condensed Matter
Publisher: The American Physical Society
Additional Information: Copyright of this article belongs to The American Physical Society.
Department/Centre: Division of Electrical Sciences > Electrical Communication Engineering
Date Deposited: 27 Dec 2010 09:17
Last Modified: 27 Dec 2010 09:17
URI: http://eprints.iisc.ac.in/id/eprint/34214

Actions (login required)

View Item View Item